High Temperature Sintered White Tabular Alumina TA 99.3% for Top Grade Refractories

1. Tabular Alumina Introduction

Tabular Alumina is a pure sintered alpha-alumina material that has been fully densified by rapid-sintering without the use of sintering aids at temperatures in excess of 1800°C.

Tabular Alumina has characteristic large, well developed hexagonal tablet shaped alpha-alumina crystals of up to 200 µm length. The excellent thermal volume stability and thermal shock characteristics can be attributed to its specific microstructure: low open porosity and large crystals with closed spherical pores,which are entrapped upon re-crystallization during rapid sintering.

2. Tabular Alumina Specifications

3. Tabular Alumina General Advantages

a. White tabular alumina is widely used in high performance refractories in the fields of iron and steel;
b. High thermal stability, good toughness;
c. Stable chemical properties;
d. The corrosion resistance of alkaline slag, slag and hot metal is good

4. Tabular Alumina Characteristics

• High refractoriness.
• Physicochemical stability.
• Bulk density high.
• Low porosity.
• Low water absorption.
• High purity and whiteness.

5. Tabular Alumina Applications
 

1. Ideal in applications such as inert catalyst bed supports
2. Regenerative burner bed applications
3. Deep bed molten aluminium filtration
4. Heat exchange media
5. Catalyst reactor
6. Desiccant bed supports
7. Ballast under exposure to high temperature

6. Tabular Alumina Particle sizes Available
 
Standard sizes: ½” - ¼”, ¼” -8, 3-6, 6-10, 6-14, 8-14, 14-28, 28-48, -14, -28, -48, -100, -325 mesh
5-10, 2-5, 3-6, 2-3, 1-3, 1-2, 0.5-1, 0.2-0.6, 0-1, 0-0.5, 0-0.3, 0-0.2, 0-0.045 mm
Other sizes available per customer's requirement.