UF Resin Multifunction Additive CT0012 Latent Curing Agent Impregnated Paper
UF Resin Multifunction Additive CT0012 Latent Curing Agent Impregnated Paper
| Color | Colorless or light yellow |
| Density | 1.150-1.250 g/ml |
| pH | 7.0-8.0 |
| Storage | can be stored at 25 ℃ for one year in a closed container. at higher temperature, the storage period decreases slightly. It may coagulate at low temperature, but its effect will not be affected after thawing. |
| Package | 200kg round plastic drum or 1000L square plastic drum |
| State | liquid |
|
Application
|
Added to the system with 0.1-0.3% weight of liquid resin, gel time is 5-10 minutes at 100℃water bath.
|
| Be used in | urea formaldehyde (UF) resin. |
|
Product Group |
Catalysts |
| Effect:wood processing | Seond stage coater latent |
| Market | Wood precessing |
| Solubilit in water | soluble |
| Boiling point | About 90-100c |
| Volatile component(%volume) | N/A |
| Relative vapor density (air＝1) | N/A |
| Heat of combustion(ºC): | N/A |
| Lower explosive limit% | Not applicable |
PRODUCT INTRODUCTION
Fenton CT0012 is a curing agent suitable for the production of impregnated paper with low pressure, it can only be used in urea formaldehyde (UF) resin.
PRODUCT PERFORMANCE
CT0012 can effectively cure UF resin, to prevent UF resin seeping to melamine resin on surface, avoiding poor surface sealing and adhesion of impregnated paper. With ct0012, temperature in the hot pressing can be increased, flow time of UF resin can be prolonged, dry / wet flaw can be reduced, the heat resistance during storage can be increased, storage time can be prolonged.
CT0012 doesn't show curing ability at room temperature (25 ℃), and active time after adding is 8-12 hours. After temporary machine maintenance , new patch of glue is not needed, saving work time. At low temperature (< 120 ℃), the curing process is slow, the resin has time spread enough, meanwhile rapid curing at high temperature provides uniformity. Dry/wer flaw, heat mark can be reduced,
Note:
in practical application of CT0012, the storage time of 50- 60% UF resin in cold storage is over 90 days.
Applications:
Added to the system with 0.1-0.3% weight of liquid resin, gel time is 5-10 minutes at 100℃water bath.
The amount of curing agent varies with the reactivity and the pH value of the resin. Before used, appropriate curing time should be determined according to the type of impregnated paper, and the accurate dosage of curing agent should be determined by lab testing.
It is suggested to be used for impregnated paper with long-time transportation and long storage time.
*Note:the curing agent should be added at last, after other additives. the curing time should be tested. Only after the curing time reaches the qualified value, can it be poured into the glue tank.
Disclaimers
The information and suggestions mentioned above are based on the experience of laboratory testing and daily use. lots of factors are involved in the manufacturing process, which are beyond our control. Therefore, the above information and suggestions could not account for every customer. We suggest adaptability test before use in batches. For the problems occurred, we only undertake the loss not greater than the value of products.