Latent Curing Agent UF Resin Decorative Paper Laminating CT0012D

Description:

Curing agent(CT0012D) is used in the production of UF resin impregnated paper.The product effectively solidifies UF resin, thus reducing the quality problems caused by UF resin leaking onto The MF surface, such as poor surface sealing, adhesion of impregnated paper and so on.

CT0012D can improve the curing temperature of impregnated paper in the process of hot pressing, prolong the resin flow time, and can improve the heat resistance temperature of impregnated paper in the process of preservation, prolong the preservation time.

FENTENG CT0012D is an organic-based catalyst designed for decorative laminating formulations.

Curing does not occur at lower temperatures(25c), and it cures quickly at high temperatures(>120c) .

Improve the clarity of decorative wood grain

Extend the active period of the UF resin stored at room temperature.

PRODUCT APPLICATION

Added to the system with 0.1-0.3% weight of liquid resin, gel time is 5-10 minutes at 100℃water bath.

The amount of curing agent varies with the reactivity and the pH value of the resin. Before used, appropriate curing time should be determined according to the type of impregnated paper, and the accurate dosage of curing agent should be determined by lab testing.

It is suggested to be used for impregnated paper with long-time transportation and long storage time.

*Note:

the curing agent should be added at last, after other additives. the curing time should be tested. Only after the curing time reaches the qualified value, can it be poured into the glue tank.