GR5 GR5ELI TC4ELI TC4 High Precision Medical Titanium Alloy Rod
| Product Name | GR5 GR5ELI TC4ELI TC4 High Precision Medical Titanium Alloy Rod |
| Specification(mm) | Dia4~100mm*(2500~3000)mm |
| Grade | TA3,TC4,TC4ELI;GR3,GR5,GR5ELI |
| Standard | ASTMF67,ASTMF136.ASTMB13810-2017 |
| Marked | Tolerance:h6~h9 or Can be processed and produced according to customer's specific specifications |
Mechanical properties reference standard:
| Grade | Mechanical properties at room temperature (≥ ) | |||
| Tensile Strength | Yield Strength | Elongation | Rate of reduction in area | |
| TA3 | 500 MPa | 380 MPa | 20% | 35% |
| TC4 (Gr5) | 930 MPa | 860 MPa | 10% | 25% |
Peakrise Metal TC4 high-precision medical titanium rod technical features: low gap TC4 and TC4 two standards in one, that is, it has the low impurities of low gap TC4 ELI and the high performance of TC4. That is to say, it has the performance characteristics of high strength and high plasticity at the same time. The following is a specific comparison of them:
Comparison of chemical composition:
|
National standard requirements
|
Al
|
V
|
Fe
|
C
|
N
|
H
|
O
|
|
TC4(standard value)
|
5.5-6.75 | 3.5-4.5 | 0.3 | 0.08 | 0.05 | 0.008 | 0.2 |
|
Tc4ELI(standard value)
|
5.5-6.5 | 3.5-4.5 | 0.25 | 0.08 | 0.03 | 0.012 | 0.13 |
Using titanium rods to make artificial bones, cells can regenerate on them and bones can grow. Titanium has good affinity with human bones, epithelium, and artificial tissue. In order to improve the surface quality of implants connected to human bones, applying a bioceramic layer to the roughened surface is also a more effective method.
Ti-6Al-4V ELI mechanical properties:
Tensile strength: >895Mpa; Yield strength: >825Mpa; Elongation after fracture: >10%; Sectional shrinkage: >25%
Macrostructure: qualified
Advantages: biocompatibility with human body, corrosion resistance, high strength