201 202 410 Astm Stainless Steel Strip Polished 1mm 2mm 3mm
Grade 410 Stainless Steel Coils/Strips
400 SERIES STAINLESS STEEL
The 400 series group of stainless steels typically have an 11% chromium and 1% manganese increase, above the 300 series group. This stainless steel series tends to be susceptible to rust and corrosion under some conditions although heat-treating will harden them. The 400 series of stainless steels have a higher carbon content, giving it a martensitic crystalline structure that provides the end product with high-strength and high-wear resistance. The 400 series steels tend to be used in agricultural equipment, gas turbine exhaust silencers, hardware, motor shafts, and more.
Type 410 is hardenable, straight-chromium stainless steels which combine superior wear resistance of high carbon alloys with the excellent corrosion resistance of chromium stainless steels. Oil quenching these alloys from temperatures between 1800°F to 1950°F (982-1066°C) produces the highest strength and/or wear resistance as well as corrosion resistance. Type 410 alloy is used where strength, hardness, and/or wear resistance must be combined with corrosion resistance
CHEMICAL COMPOSITION
| Element | C | Mn | Cr | Ni | P | S | Si |
| 409 | 0.03% | 1.00% | 10.5~11.7% | 0.50% | 0.04% | 0.02% | 1.00% |
| 410 | 0.08~0.15% | 1.00% | 11.5~13.5% | 0.75% | 0.04% | 0.03% | 1.00% |
| 420 | 0.15% | 1.00% | 12.0~14.0% | - | 0.04% | 0.03% | 1.00% |
| 430 | 0.12% | 1.00% | 16.0~18.0% | 0.75% | 0.04% | 0.03% | 1.00% |
MECHANICAL PROPERTIES
| Grade |
Tensile Strength (MPa) Min |
Yield Strength 0.2% proof (MPa) Min |
Elongation (%in 50mm) Min |
Rockwell B(HRB) Max |
| 410 |
510
|
290 | 34 | 82-96 |
410 COMMON APPLICATIONS
The typical applications of grade 410 stainless steels are listed below:
- Bolts, screws, bushings and nuts.
- Petroleum fractionating structures.
- Shafts, pumps and valves.
- Mine ladder rungs.
- Gas turbines