S-Plastic Thermocomp PF0069 is a compound based on PA 6 resin containing Glass Fiber, Flame Retardant. Added features includ

Name: S-Plastic Thermocomp PF0069 is a compound based on PA 6 resin containing Glass Fiber, Flame Retardant. Added features includ
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp PF0069 resin is a compound based on PA 6 resin containing Glass Fiber, Flame Retardant. Added features include; Flame

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, break, 5 mm/min	150	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.5	%	ISO 527
Tensile Modulus, 1 mm/min	10000	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	225	MPa	ISO 178
Flexural Stress, break, 2 mm/min	223	MPa	ISO 178
Flexural Strain, break, 2 mm/min	3.1	%	ISO 178
Flexural Modulus, 2 mm/min	9600	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched 80104 +23°C	65	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	11	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	195	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Mold Shrinkage, flow	0.2	%	S-Plastics Method
Density	1.64	g/cm³	ISO 1183
Water Absorption, 23°C/24hrs	1	%	ISO 62-1
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Compliant, 94V-0 Flame Class Rating (3)(4)	1.6	mm	UL 94 by GE

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	255 - 265	°C
Front - Zone 3 Temperature	250 - 260	°C
Middle - Zone 2 Temperature	250 - 260	°C
Rear - Zone 1 Temperature	245 - 255	°C
Mold Temperature	55 - 95	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:11/28/2008