S-Plastic Thermocomp Lexan_EXCP0021 resin compound is a 40% glass reinforced injection moulding polycarbonate resin.

Name: S-Plastic Thermocomp Lexan_EXCP0021 resin compound is a 40% glass reinforced injection moulding polycarbonate resin.
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp Lexan_EXCP0021 resin compound is a 40% glass reinforced injection moulding polycarbonate resin.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, break, 5 mm/min	130	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.6	%	ISO 527
Flexural Stress, break, 2 mm/min	195	MPa	ISO 178
Flexural Modulus, 2 mm/min	10500	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched 80104 +23°C	35	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	12	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/120	143	°C	ISO 306
PHYSICAL	Value	Unit	Standard
Density	1.5	g/cm³	ISO 1183
Melt Volume Rate, MVR at 300°C/1.2 kg	9	cm³/10 min	ISO 1133
Source GMD, last updated:02/12/2001

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	2 - 4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	290 - 320	°C
Nozzle Temperature	280 - 310	°C
Front - Zone 3 Temperature	290 - 320	°C
Middle - Zone 2 Temperature	280 - 310	°C
Rear - Zone 1 Temperature	270 - 300	°C
Hopper Temperature	60 - 80	°C
Mold Temperature	80 - 120	°C
Source GMD, last updated:02/12/2001