S-Plastic Thermocomp Lexan_EXCP0022 resin 11% carbon fiber filled PC injection moulding resin. Material identification a

Name: S-Plastic Thermocomp Lexan_EXCP0022 resin 11% carbon fiber filled PC injection moulding resin. Material identification a
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp Lexan_EXCP0022 resin is a 11% carbon fiber filled PC injection moulding resin. Material identification acc.
ISO11469: >PC-CF11<

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yield, 5 mm/min	105	MPa	ISO 527
Tensile Strain, break, 5 mm/min	5	%	ISO 527
Tensile Modulus, 1 mm/min	7500	MPa	ISO 527
IMPACT	Value	Unit	Standard
Izod Impact, notched 80104 +23°C	6	kJ/m²	ISO 180/1A
Charpy 23°C, Unnotch Edgew 80104 sp=62mm	30	kJ/m²	ISO 179/1eU
THERMAL	Value	Unit	Standard
HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm	136	°C	ISO 75/Ae
PHYSICAL	Value	Unit	Standard
Density	1.24	g/cm³	ISO 1183
Melt Volume Rate, MVR at 300°C/1.2 kg	20	cm³/10 min	ISO 1133
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Compliant, 94HB Flame Class Rating (3)(4)	0.8	mm	UL 94 by GE
Source GMD, last updated:01/08/2002

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	4 - 6	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	285 - 310	°C
Nozzle Temperature	295 - 310	°C
Front - Zone 3 Temperature	295 - 310	°C
Middle - Zone 2 Temperature	295 - 305	°C
Rear - Zone 1 Temperature	275 - 295	°C
Hopper Temperature	60 - 80	°C
Mold Temperature	70 - 100	°C
Source GMD, last updated:01/08/2002