S-Plastic Thermocomp Lexan_SML5750 resin is 50% glass bead and filament reinforced. 270F HDT. Will be commercialized as LGB5

Name: S-Plastic Thermocomp Lexan_SML5750 resin is 50% glass bead and filament reinforced. 270F HDT. Will be commercialized as LGB5
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Thermocomp

Product Description

S-Plastics Thermocomp Lexan_SML5750 resin is 50% glass bead and filament reinforced. 270F HDT. Will be commercialized as LGB5030N.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	124	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	144	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	4.9	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	5	%	ASTM D 638
Tensile Modulus, 5 mm/min	11030	MPa	ASTM D 638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	178	MPa	ASTM D 790
Flexural Stress, brk, 2.6 mm/min, 100 mm span	197	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	10820	MPa	ASTM D 790
Flexural Modulus, 2.6 mm/min, 100 mm span	10110	MPa	ASTM D 790
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	534	J/m	ASTM D 4812
Izod Impact, notched, 23°C	96	J/m	ASTM D 256
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	137	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	132	°C	ASTM D 648
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.63	-	ASTM D 792
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94HB Flame Class Rating (3)	1.49	mm	UL 94
UL Recognized, 94V-1 Flame Class Rating (3)	2.99	mm	UL 94
Source GMD, last updated:12/28/1999

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	48	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	315 - 340	°C
Nozzle Temperature	310 - 330	°C
Front - Zone 3 Temperature	315 - 340	°C
Middle - Zone 2 Temperature	305 - 325	°C
Rear - Zone 1 Temperature	295 - 315	°C
Mold Temperature	80 - 115	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm
Source GMD, last updated:12/28/1999