S-Plastic Valox EXVX1254 Alox IQ IQ3001 Unfilled PBT Modified With Elastomer Targeted For Flexible Hinge Applications

Name: S-Plastic Valox EXVX1254 Alox IQ IQ3001 Unfilled PBT Modified With Elastomer Targeted For Flexible Hinge Applications
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Valox

Product Description

S-Plastics Valox EXVX1254 resin is Valox IQ IQ3001 - Unfilled PBT modified with elastomer. Targeted for flexible hinge applications.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	48	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	48	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	5	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	120	%	ASTM D 638
Tensile Modulus, 5 mm/min	2300	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	82	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	2060	MPa	ASTM D 790
Tensile Stress, yield, 50 mm/min	50	MPa	ISO 527
Tensile Stress, break, 50 mm/min	50	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Tensile Strain, break, 50 mm/min	120	%	ISO 527
Tensile Modulus, 1 mm/min	2300	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	75	MPa	ISO 178
Flexural Modulus, 2 mm/min	2200	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	53	J/m	ASTM D 256
Izod Impact, notched 80104 +23°C	5	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 1.82 MPa, 3.2mm, unannealed	48	°C	ASTM D 648
HDT, 0.45 MPa, 6.4 mm, unannealed	148	°C	ASTM D 648
CTE, -40°C to 40°C, flow	9.18E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	9.18E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/120	155	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	48	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.31	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	2.1 - 2.3	%	S-Plastics Method
Melt Flow Rate, 250°C/1.2 kgf	21	g/10 min	ASTM D 1238
Density	1.3	g/cm³	ISO 1183
Water Absorption, (23°C/sat)	0.08	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.08	%	ISO 62
Melt Volume Rate, MVR at 250°C/1.2 kg	20	cm³/10 min	ISO 1133
Source GMD, last updated:01/04/2007

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	12	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	250 - 265	°C
Nozzle Temperature	245 - 260	°C
Front - Zone 3 Temperature	250 - 265	°C
Middle - Zone 2 Temperature	245 - 260	°C
Rear - Zone 1 Temperature	240 - 255	°C
Mold Temperature	65 - 90	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	50 - 80	rpm
Shot to Cylinder Size	40 - 80	%
Vent Depth	0.025 - 0.038	mm
Source GMD, last updated:01/04/2007