S-Plastic Valox 310HP resin Is Unreinforced Neat Resin For Compounding Only Not Intended For Injection Molding
Price:
*USD
MOQ:
100KG
Delivery Time:
To be negotiated
Brand:
S-Plastic Valox
Product Description
S-Plastics Valox 310HPresin is Unreinforced, neat resin for compounding only. Not intended for injection molding. Medium viscosity 5000-7000 P. Available in natural(1001) color. FDA Food Contact Compliant
Property
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 51 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 50 mm/min | 51 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 50 mm/min | 3.5 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 200 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2400 | MPa | ASTM D 638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 82 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2340 | MPa | ASTM D 790 |
| Hardness, Rockwell R | 117 | - | ASTM D 785 |
| Tensile Stress, yield, 50 mm/min | 57 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 57 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 3.5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 80 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2650 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 81 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2290 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1602 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 53 | J/m | ASTM D 256 |
| Izod Impact, notched, -30°C | 32 | J/m | ASTM D 256 |
| Modified Gardner, 23°C | 40 | J | ASTM D 3029 |
| Instrumented Impact Total Energy, 23°C | 24 | J | ASTM D 3763 |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 3 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 170 | °C | ASTM D 1525 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 52 | °C | ASTM D 648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 154 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 54 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 8.1E-05 | 1/°C | ASTM E 831 |
| CTE, 60°C to 138°C, flow | 1.39E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 1.2E-04 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 1.3E-04 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | Pass | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 170 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 170 | °C | ISO 306 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 51 | °C | ISO 75/Af |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.31 | - | ASTM D 792 |
| Specific Volume | 0.76 | cm³/g | ASTM D 792 |
| Water Absorption, 24 hours | 0.08 | % | ASTM D 570 |
| Mold Shrinkage, flow, 3.2 mm | 1.2 - 1.3 | % | S-Plastics Method |
| Mold Shrinkage, flow, 0.75-2.3 mm | 0.9 - 1.6 | % | S-Plastics Method |
| Mold Shrinkage, flow, 2.3-4.6 mm | 1.5 - 2.3 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 0.75-2.3 mm | 1 - 1.7 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 2.3-4.6 mm | 1.6 - 2.4 | % | S-Plastics Method |
| Melt Flow Rate, 250°C/5.0 kgf | 34.6 | g/10 min | ASTM D 1238 |
| Density | 1.31 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.08 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 |
| Melt Volume Rate, MVR at 250°C/5.0 kg | 33 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >4.E+16 | Ohm-cm | ASTM D 257 |
| Dielectric Strength, in air, 3.2 mm | 15.7 | kV/mm | ASTM D 149 |
| Dielectric Strength, in oil, 1.6 mm | 23.2 | kV/mm | ASTM D 149 |
| Relative Permittivity, 100 Hz | 3.3 | - | ASTM D 150 |
| Relative Permittivity, 1 MHz | 3.1 | - | ASTM D 150 |
| Dissipation Factor, 100 Hz | 0.002 | - | ASTM D 150 |
| Dissipation Factor, 1 kHz | 0.4193 | - | ASTM D 150 |
| Dissipation Factor, 1 MHz | 0.02 | - | ASTM D 150 |
| Source GMD, last updated:05/12/2006 | |||
Processing
| Parameter | ||
| Compounding Extrusion | Value | Unit |
| Drying Temperature | 110 - 120 | °C |
| Drying Time | 4 - 6 | hrs |
| Drying Time (Cumulative) | 8 | hrs |
| Maximum Moisture Content | 0 | % |
| Melt Temperature | 245 - 260 | °C |
| Barrel - Zone 1 Temperature | 200 - 230 | °C |
| Barrel - Zone 2 Temperature | 240 - 255 | °C |
| Barrel - Zone 3 Temperature | 240 - 275 | °C |
| Barrel - Zone 4 Temperature | 240 - 275 | °C |
| Adapter Temperature | 240 - 275 | °C |
| Die Temperature | 240 - 275 | °C |
| Waterbath Temperature | 25 - 35 | °C |
| Source GMD, last updated:05/12/2006 | ||
|
For more information please download the datasheet |
|
 |
|
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
SAMTION INTERNATIONAL LIMITED
Location
Room 803B, 8/F., West Coast International Building, 290-296 Un Chau Street, Cheung Sha Wan, Kowloon, Hong Kong
Contact Person
Justin