S-Plastic Valox 365 resin Is Unreinforced Opaque Provides Chemical Resistance And Dimensional Stability UL94V-0 Rated

Name: S-Plastic Valox 365 resin Is Unreinforced Opaque Provides Chemical Resistance And Dimensional Stability UL94V-0 Rated
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Valox

Product Description

S-Plastics Valox 365 resin is Unreinforced, opaque, provides chemical resistance and dimensional stability, UL94V-0 rated at 0.031".

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	41	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	41	MPa	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	120	%	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	68	MPa	ASTM D 790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	68	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	2240	MPa	ASTM D 790
Hardness, Rockwell R	115	-	ASTM D 785
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	640	J/m	ASTM D 256
Izod Impact, notched, -30°C	192	J/m	ASTM D 256
Izod Impact, notched, -40°C	170	J/m	ASTM D 256
Gardner, 23°C	37	J	ASTM D 3029
Modified Gardner, 23°C	37	J	ASTM D 3029
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 6.4 mm, unannealed	129	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed	121	°C	ASTM D 648
CTE, -40°C to 40°C, flow	6.84E-05	1/°C	ASTM E 831
CTE, -40°C to 95°C, flow	7.92E-05	1/°C	ASTM E 831
CTE, 60°C to 138°C, flow	8.28E-05	1/°C	ASTM E 831
Relative Temp Index, Elec	105	°C	UL 746B
Relative Temp Index, Mech w/impact	105	°C	UL 746B
Relative Temp Index, Mech w/o impact	105	°C	UL 746B
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.33	-	ASTM D 792
Specific Volume	0.75	cm³/g	ASTM D 792
Water Absorption, 24 hours	0.14	%	ASTM D 570
Water Absorption, equilibrium, 23C	0.6	%	ASTM D 570
Mold Shrinkage, flow, 0.75-2.3 mm	0.8 - 1.1	%	S-Plastics Method
Mold Shrinkage, flow, 2.3-4.6 mm	1 - 1.4	%	S-Plastics Method
Mold Shrinkage, xflow, 0.75-2.3 mm	0.9 - 1.3	%	S-Plastics Method
Mold Shrinkage, xflow, 2.3-4.6 mm	1.2 - 1.6	%	S-Plastics Method
ELECTRICAL	Value	Unit	Standard
Dielectric Strength, in oil, 3.2 mm	12	kV/mm	ASTM D 149
Relative Permittivity, 100 Hz	8.5	-	ASTM D 150
Relative Permittivity, 1 MHz	5.7	-	ASTM D 150
Dissipation Factor, 100 Hz	0.002	-	ASTM D 150
Dissipation Factor, 1 MHz	0.03	-	ASTM D 150
Arc Resistance, Tungsten {PLC}	6	PLC Code	ASTM D 495
Hot Wire Ignition {PLC)	2	PLC Code	UL 746A
High Voltage Arc Track Rate {PLC}	3	PLC Code	UL 746A
High Ampere Arc Ign, surface {PLC}	3	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	3	PLC Code	UL 746A
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94V-0 Flame Class Rating (3)	0.76	mm	UL 94
UL Recognized, 94-5VA Rating (3)	2.2	mm	UL 94
CSA (See File for complete listing)	LS88480	File No.	CSA LISTED
Oxygen Index (LOI)	28.8	%	ASTM D 2863
UV-light, water exposure/immersion	F2	-	UL 746C
Source GMD, last updated:01/03/2006

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120	°C
Drying Time	3 - 4	hrs
Drying Time (Cumulative)	12	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	250 - 265	°C
Nozzle Temperature	245 - 260	°C
Front - Zone 3 Temperature	250 - 265	°C
Middle - Zone 2 Temperature	245 - 260	°C
Rear - Zone 1 Temperature	240 - 255	°C
Mold Temperature	50 - 75	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	50 - 100	rpm
Shot to Cylinder Size	40 - 80	%
Vent Depth	0.025 - 0.038	mm
Source GMD, last updated:01/03/2006