China S-Plastic Valox FV620 Data For 10% Weight Reduction At 0.250

S-Plastic Valox FV620 Data For 10% Weight Reduction At 0.250" Wall 30% GR Excellent Heat/Chemical Resistance

Name: S-Plastic Valox FV620 Data For 10% Weight Reduction At 0.250 Wall 30% GR Excellent Heat/Chemical Resistance
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Valox

Product Description

S-Plastics Valox FV620 resin is Data for 10% weight reduction at 0.250" wall, 30% GR. Excellent heat/chemical resistance, high flex mod. V-0 at 0.157" (3.99 mm).

Property

MECHANICAL	Value	Unit	Standard
FOAM - MECHANICAL 6.4 mm Wt Reduction	10	%	-
Tensile Stress, yield, 6.35 mm	77	MPa	ASTM D 638
Tensile Strain, break, 6.35 mm	4.8	%	ASTM D 638
Tensile Modulus, 6.4 mm	8370	MPa	ASTM D 638
Flexural Stress, yield, 6.4 mm	146	MPa	ASTM D 790
Flexural Modulus, 6.4 mm	7650	MPa	ASTM D 790
IMPACT	Value	Unit	Standard
FOAM - IMPACT 6.4 mm Wt Reduction	10	%	-
Izod Impact, unnotched, 23°C	534	J/m	ASTM D 4812
Falling Dart Impact, 23°C	14	J	S-Plastics Method
THERMAL	Value	Unit	Standard
FOAM - THERMAL 6.4mm Wt Reduction	10	%	-
HDT, 0.45 MPa, 6.4 mm, unannealed	201	°C	ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed	140	°C	ASTM D 648
CTE, -40°C to 95°C, flow	2.34E-05	1/°C	ASTM E 831
Specific Heat	1.15	J/g-°C	ASTM C 351
Thermal Conductivity	0.16	W/m-°C	ASTM C 177
Relative Temp Index, Elec	75	°C	UL 746B
Relative Temp Index, Mech w/impact	75	°C	UL 746B
Relative Temp Index, Mech w/o impact	75	°C	UL 746B
PHYSICAL	Value	Unit	Standard
FOAM - PHYSICAL 6.4mm Wt Reduction	10	%	-
Specific Gravity	1.62	-	ASTM D 792
Specific Gravity, foam molded	1.46	-	ASTM D 792
Water Absorption, 24 hours	0.04	%	ASTM D 570
Water Absorption, equilibrium, 23C	0.09	%	ASTM D 570
Mold Shrinkage, flow, 6.4 mm	0.3 - 0.5	%	S-Plastics Method
ELECTRICAL	Value	Unit	Standard
FOAM - ELECTRICAL 6.4 mm Wt Reduction	20	%	-
Volume Resistivity	2.5E+17	Ohm-cm	ASTM D 257
Surface Resistivity	>1.1E+17	Ohm	ASTM D 257
Relative Permittivity, 100 Hz	3.09	-	ASTM D 150
Relative Permittivity, 1 MHz	2.94	-	ASTM D 150
Dissipation Factor, 100 Hz	0.004	-	ASTM D 150
Dissipation Factor, 1 MHz	0.011	-	ASTM D 150
Arc Resistance, Tungsten {PLC}	7	PLC Code	ASTM D 495
Hot Wire Ignition {PLC)	2	PLC Code	UL 746A
High Voltage Arc Track Rate {PLC}	2	PLC Code	UL 746A
High Ampere Arc Ign, surface {PLC}	2	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	3	PLC Code	UL 746A
FLAME CHARACTERISTICS	Value	Unit	Standard
FOAM - Flame Class Minimum Density	1.2	g/cm³	-
UL Recognized, 94V-0 Flame Class Rating (3)	3.91	mm	UL 94
UL Recognized, 94-5VA Rating (3)	4.9	mm	UL 94
Source GMD, last updated:08/09/1989

Processing

THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.