S-Plastic Valox SHF4960 Valox Super High Flow Grade 30% Glass Filled Flame Retardant High CTI Heat Stabilized

Name: S-Plastic Valox SHF4960 Valox Super High Flow Grade 30% Glass Filled Flame Retardant High CTI Heat Stabilized
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Valox

Product Description

S-Plastics Valox SHF4960 resin isValox Super high flow grade, 30% glass filled Flame retardant, High CTI, heat stabilized with mold release.

Property

MECHANICAL Value Unit Standard

Tensile Stress, yield, 5 mm/min 110 MPa ISO 527

Tensile Stress, break, 5 mm/min 110 MPa ISO 527

Tensile Strain, yield, 5 mm/min 1.8 % ISO 527

Tensile Strain, break, 5 mm/min 1.8 % ISO 527

Tensile Modulus, 1 mm/min 10000 MPa ISO 527

Flexural Stress, yield, 2 mm/min 165 MPa ISO 178

Flexural Modulus, 2 mm/min 8500 MPa ISO 178

IMPACT Value Unit Standard

Izod Impact, unnotched 80*10*4 -30°C 36 kJ/m² ISO 180/1U

Izod Impact, notched 80*10*4 +23°C 7 kJ/m² ISO 180/1A

Izod Impact, notched 80*10*4 -30°C 7 kJ/m² ISO 180/1A

Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm 7 kJ/m² ISO 179/1eA

THERMAL Value Unit Standard

CTE, -40°C to 40°C, flow 2.5E-05 1/°C ISO 11359-2

CTE, -40°C to 40°C, xflow 1.2E-04 1/°C ISO 11359-2

Vicat Softening Temp, Rate B/50 185 °C ISO 306

Vicat Softening Temp, Rate B/120 195 °C ISO 306

HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 195 °C ISO 75/Af

PHYSICAL Value Unit Standard

Density 1.64 g/cm³ ISO 1183

Water Absorption, (23°C/sat) 0.25 % ISO 62

Moisture Absorption (23°C / 50% RH) 0.07 % ISO 62

Melt Volume Rate, MVR at 250°C/2.16 kg 6 cm³/10 min ISO 1133

Melt Viscosity, 250°C, 1500 sec-1 92 Pa-s ISO 11443

ELECTRICAL Value Unit Standard

Volume Resistivity >1.E+15 Ohm-cm IEC 60093

Surface Resistivity, ROA >1.E+12 Ohm IEC 60093

Dielectric Strength, in oil, 0.8 mm 35 kV/mm IEC 60243-1

Dielectric Strength, in oil, 1.6 mm 24.5 kV/mm IEC 60243-1

Dielectric Strength, in oil, 3.2 mm 17.8 kV/mm IEC 60243-1

Comparative Tracking Index 275 V IEC 60112

FLAME CHARACTERISTICS Value Unit Standard

UL Compliant, 94V-0 Flame Class Rating (3)(4) 0.8 mm UL 94 by GE

Oxygen Index (LOI) 32 % ISO 4589

Source GMD, last updated:12/21/2006

Processing

Injection Molding	Value	Unit
Drying Temperature	110 - 120	°C
Drying Time	2 - 4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	250 - 270	°C
Nozzle Temperature	240 - 260	°C
Front - Zone 3 Temperature	245 - 265	°C
Middle - Zone 2 Temperature	240 - 255	°C
Rear - Zone 1 Temperature	230 - 245	°C
Hopper Temperature	40 - 60	°C
Mold Temperature	40 - 100	°C
Source GMD, last updated:12/21/2006
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.