S-Plastic Valox V3109HR Hydrolytically Resistant High Flow Polyester Grade
Price:
*USD
MOQ:
100KG
Delivery Time:
To be negotiated
Brand:
S-Plastic Valox
Product Description
S-Plastics Valox V3109HR resin is Hydrolytically resistant high flow polyester grade.
Property
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 50 mm/min | 55 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 50 mm/min | 200 | % | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 86 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2410 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 1602 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 53 | J/m | ASTM D 256 |
| THERMAL | Value | Unit | Standard |
| HDT, 1.82 MPa, 3.2mm, unannealed | 52 | °C | ASTM D 648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 148 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 8.64E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 95°C, flow | 1.19E-04 | 1/°C | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.31 | - | ASTM D 792 |
| Specific Volume | 0.1 | cm³/g | ASTM D 792 |
| Water Absorption, 24 hours | 0.06 | % | ASTM D 570 |
| Mold Shrinkage, flow, 3.2 mm | 2.1 - 2.3 | % | S-Plastics Method |
| Mold Shrinkage on Tensile Bar, xflow (2) | 2.2 - 2.4 | % | S-Plastics Method |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 2.5E+16 | Ohm-cm | ASTM D 257 |
| Dielectric Strength, in air, 3.2 mm | 16.9 | kV/mm | ASTM D 149 |
| Relative Permittivity, 50/60 Hz | 2.9 | - | ASTM D 150 |
| Relative Permittivity, 1 MHz | 2.88 | - | ASTM D 150 |
| Dissipation Factor, 50/60 Hz | 0.001 | - | ASTM D 150 |
| Dissipation Factor, 1 MHz | 0.016 | - | ASTM D 150 |
| Source GMD, last updated:04/07/2001 | |||
Processing
Injection Molding Value Unit
Drying Temperature 60 - 75 °C
Drying Time 4 - 5 hrs
Drying Time (Cumulative) 8 hrs
Maximum Moisture Content 0.05 %
Melt Temperature 250 - 265 °C
Nozzle Temperature 245 - 260 °C
Front - Zone 3 Temperature 250 - 265 °C
Middle - Zone 2 Temperature 245 - 260 °C
Rear - Zone 1 Temperature 240 - 255 °C
Mold Temperature 65 - 90 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 50 - 80 rpm
Shot to Cylinder Size 40 - 80 %
Vent Depth 0.025 - 0.038 mm
Source GMD, last updated:04/07/2001
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION
"(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours
storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded
samples. All samples tested under ISO test standards are prepared according to ISO 294."
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
|
For more information please download the datasheet |
|
 |
|
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.