S-Plastics Valox IQNH4550 resin is a non-brominated/non-chlorinated flame retardant product based on an environmentally sustainable Valox iQ*

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	104	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	104	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	2	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	2	%	ASTM D 638
Tensile Modulus, 5 mm/min	11000	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	157	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	9370	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	105	MPa	ISO 527
Tensile Stress, break, 5 mm/min	105	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	2	%	ISO 527
Tensile Strain, break, 5 mm/min	2	%	ISO 527
Tensile Modulus, 1 mm/min	10420	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	159	MPa	ISO 178
Flexural Modulus, 2 mm/min	9350	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	49	J/m	ASTM D 256
Izod Impact, notched, -30°C	46	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	6	J	ASTM D 3763
Izod Impact, unnotched 80103 +23°C	35	kJ/m²	ISO 180/1U
Izod Impact, unnotched 80104 -30°C	32	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	6	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	5	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm	5	kJ/m²	ISO 179/1eA
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	200	°C	ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed	190	°C	ASTM D 648
CTE, -40°C to 150°C, flow	2.3E+01	1/°C	ASTM E 831
CTE, -40°C to 150°C, xflow	7.8E+01	1/°C	ASTM E 831
CTE, -30°C to 80°C, flow	2.8E+01	1/°C	ISO 11359-2
CTE, -30°C to 80°C, xflow	1.05E+02	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	200	°C	ISO 306
Vicat Softening Temp, Rate B/120	200	°C	ISO 306
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	190	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.53	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.4 - 0.9	%	S-Plastics Method
Mold Shrinkage, xflow, 3.2 mm	0.8 - 1.3	%	S-Plastics Method
Melt Flow Rate, 250°C/5.0 kgf	20	g/10 min	ASTM D 1238
Density	1.52	g/cm³	ISO 1183
Water Absorption, (23°C/sat)	0.25	%	ISO 62
Moisture Absorption (23°C / 50% RH)	0.07	%	ISO 62
Melt Volume Rate, MVR at 250°C/5.0 kg	15	cm³/10 min	ISO 1133
ELECTRICAL	Value	Unit	Standard
Hot Wire Ignition {PLC)	0	PLC Code	UL 746A
High Ampere Arc Ign, surface {PLC}	0	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	2	PLC Code	UL 746A
Comparative Tracking Index	275	V	IEC 60112
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Recognized, 94V-0 Flame Class Rating (3)	0.8	mm	UL 94
UL Recognized, 94-5VA Rating (3)	3	mm	UL 94
Glow Wire Flammability Index 960°C, passes at	0.8	mm	IEC 60695-2-12
Glow Wire Ignitability Temperature, 3.0 mm	800	°C	IEC 60695-2-13
Source GMD, last updated:12/01/2008

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	110 - 120	°C
Drying Time	2 - 4	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	245 - 260	°C
Nozzle Temperature	230 - 255	°C
Front - Zone 3 Temperature	240 - 260	°C
Middle - Zone 2 Temperature	235 - 250	°C
Rear - Zone 1 Temperature	230 - 240	°C
Hopper Temperature	40 - 60	°C
Mold Temperature	40 - 100	°C
Source GMD, last updated:12/01/2008