S-Plastic Valox V8060RE 30% Glass Reinforced PBT+PET Blend With 25% Post-Consumer Recycle Hydrolitically Stable
Price:
*USD
MOQ:
100KG
Delivery Time:
To be negotiated
Brand:
S-Plastic Valox
Product Description
S-Plastics Valox V8060RE resin is 30% glass reinforced PBT+PET blend with 25% post-consumer recycle. Hydrolitically stable. Auto specs for GM, Ford, Chrysler.
Property
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yld, Type I, 5 mm/min | 106 | MPa | ASTM D 638 |
| Tensile Stress, brk, Type I, 5 mm/min | 106 | MPa | ASTM D 638 |
| Tensile Strain, yld, Type I, 5 mm/min | 3.8 | % | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3.8 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 7230 | MPa | ASTM D 638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 169 | MPa | ASTM D 790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7060 | MPa | ASTM D 790 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | 747 | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | 85 | J/m | ASTM D 256 |
| Instrumented Impact Total Energy, 23°C | 6 | J | ASTM D 3763 |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp, Rate B/50 | 190 | °C | ASTM D 1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 207 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 171 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 2.88E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 6.84E-05 | 1/°C | ASTM E 831 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.53 | - | ASTM D 792 |
| Mold Shrinkage, flow, 3.2 mm | 0.25 - 0.55 | % | S-Plastics Method |
| Mold Shrinkage, xflow, 3.2 mm | 0.55 - 0.85 | % | S-Plastics Method |
| Melt Flow Rate, 266°C/5.0 kgf | 32 | g/10 min | ASTM D 1238 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.6E+16 | Ohm-cm | ASTM D 257 |
| Dielectric Strength, in oil, 3.2 mm | 15.7 | kV/mm | ASTM D 149 |
| Relative Permittivity, 100 Hz | 3.4 | - | ASTM D 150 |
| Relative Permittivity, 1 MHz | 3.3 | - | ASTM D 150 |
| Dissipation Factor, 100 Hz | 0.0026 | - | ASTM D 150 |
| Dissipation Factor, 1 MHz | 0.0155 | - | ASTM D 150 |
| AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS III | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 98 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.8 | % | ASTM D 638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7630 | MPa | ASTM D 790 |
| Instrumented Impact, Total Energy, 23°C | 6 | J | ASTM D 3763 |
| AFTER 40 CYCLES, SIMILAR TO USCAR-2, CLASS IV | Value | Unit | Standard |
| Tensile Stress, brk, Type I, 5 mm/min | 107 | MPa | ASTM D 638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.9 | % | ASTM D 638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7940 | MPa | ASTM D 790 |
| Instrumented Impact, Total Energy, 23°C | 5 | J | ASTM D 3763 |
Processing
Injection Molding Value Unit
Drying Temperature 60 - 75 °C
Drying Time 4 - 5 hrs
Drying Time (Cumulative) 8 hrs
Maximum Moisture Content 0.05 %
Minimum Moisture Content 0.02 %
Melt Temperature 255 - 275 °C
Nozzle Temperature 255 - 270 °C
Front - Zone 3 Temperature 255 - 265 °C
Middle - Zone 2 Temperature 250 - 260 °C
Rear - Zone 1 Temperature 245 - 255 °C
Mold Temperature 65 - 95 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 50 - 80 rpm
Shot to Cylinder Size 30 - 80 %
Vent Depth 0.025 - 0.038 mm
Source GMD, last updated:02/28/2002
• If material is stored in dryer for extended periods (overnight or more):
Lower dryer temperature to room temperature.
Recirculate cool dry air over material.
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION
"(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours
storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded
samples. All samples tested under ISO test standards are prepared according to ISO 294."
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.
|
For more information please download the datasheet |
|
 |
|
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
SAMTION INTERNATIONAL LIMITED
Location
Room 803B, 8/F., West Coast International Building, 290-296 Un Chau Street, Cheung Sha Wan, Kowloon, Hong Kong
Contact Person
Justin