S-Plastic Valox V9540CS Is A Flame Retardant 20% Glass Filled PET Injection Moulding Resin

Name: S-Plastic Valox V9540CS Is A Flame Retardant 20% Glass Filled PET Injection Moulding Resin
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Valox

Product Description

S-Plastics Valox V9540CS resin is a flame retardant, 20% glass filled PET injection moulding resin with good color stability and good heat resistance.

Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, break, 5 mm/min	135	MPa	ISO 527
Tensile Strain, break, 50 mm/min	2	%	ISO 527
Tensile Modulus, 1 mm/min	9500	MPa	ISO 527
Flexural Stress, break, 2 mm/min	185	MPa	ISO 178
Flexural Modulus, 2 mm/min	8500	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched 80104 +23°C	32	kJ/m²	ISO 180/1U
THERMAL	Value	Unit	Standard
Ball Pressure Test, 125°C +/- 2°C	PASSES	-	IEC 60695-10-2
Ball Pressure Test, approximate maximum	245	°C	IEC 60695-10-2
Vicat Softening Temp, Rate B/120	230	°C	ISO 306
PHYSICAL	Value	Unit	Standard
Mold Shrinkage on Tensile Bar, flow (2)	0.2 - 0.4	%	S-Plastics Method
Density	1.68	g/cm³	ISO 1183
Melt Volume Rate, MVR at 265°C/2.16 kg	8	cm³/10 min	ISO 1133
ELECTRICAL	Value	Unit	Standard
Comparative Tracking Index	175	V	IEC 60112
FLAME CHARACTERISTICS	Value	Unit	Standard
Glow Wire Flammability Index 960°C, passes at	1.6	mm	IEC 60695-2-12
Source GMD, last updated:05/28/2003

Processing

Injection Molding	Value	Unit
Drying Temperature	120 - 130	°C
Drying Time	4 - 6	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	270 - 290	°C
Nozzle Temperature	260 - 280	°C
Front - Zone 3 Temperature	270 - 290	°C
Middle - Zone 2 Temperature	260 - 280	°C
Rear - Zone 1 Temperature	250 - 270	°C
Hopper Temperature	40 - 60	°C
Mold Temperature	90 - 120	°C
Source GMD, last updated:05/28/2003
THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES.
PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION
(1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294.
(2) Only typical data for selection purposes. Not to be used for part or tool design.
(3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions.
(4) Internal measurements according to UL standards.