S-Plastic Valox VX8015U Is A UV Stabilized 15% Glass Reinforced PBT+PET Injection Moulding Resin With Improved Surface
Price:
*USD
MOQ:
100KG
Delivery Time:
To be negotiated
Brand:
S-Plastic Valox
Product Description
S-Plastics Valox VX8015U resin is a UV stabilized, 15% glass reinforced PBT+PET injection moulding resin with improved surface finish quality
characteristics versus VALOX 815. This grade is 815 with improved gloss and improved UV performance.
Property
| MECHANICAL | Value | Unit | Standard |
| Taber Abrasion, CS-17, 1 kg | 17 | mg/1000cy | S-Plastics Method |
| Tensile Stress, break, 5 mm/min | 90 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 6000 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 135 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 5000 | MPa | ISO 178 |
| Hardness, H358/30 | 101 | MPa | ISO 2039-1 |
| Hardness, Rockwell R | 119 | - | ISO 2039-2 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | 25 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 25 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA |
| Charpy Impact, notched, 23°C | 6 | kJ/m² | ISO 179/2C |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| Charpy Impact, notched, -20°C | 6 | kJ/m² | ISO 179/2C |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| CTE, 23°C to 80°C, flow | 5.5E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 8.5E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 220 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 200 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 213 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 215 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 175 | °C | ISO 75/Ae |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.4 - 0.8 | % | S-Plastics Method |
| Mold Shrinkage on Tensile Bar, xflow (2) | 0.6 - 1 | % | S-Plastics Method |
| Density | 1.43 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 0.26 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 |
| Melt Volume Rate, MVR at 265°C/1.2 kg | 12 | cm³/10 min | ISO 1133 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 |
| Dielectric Strength, shorttime, 1.0mm | 18 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 0.8 mm | 30 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 1.6 mm | 24 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 50/60 Hz | 3 | - | IEC 60250 |
| Relative Permittivity, 100 Hz | 3.6 | - | IEC 60250 |
| Relative Permittivity, 1 MHz | 2.9 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.001 | - | IEC 60250 |
| Dissipation Factor, 100 Hz | 0.002 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.014 | - | IEC 60250 |
| Comparative Tracking Index | 325 | V | IEC 60112 |
| Comparative Tracking Index, M | 175 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant, 94HB Flame Class Rating (3)(4) | 1.6 | mm | UL 94 by GE |
| Glow Wire Flammability Index 750°C, passes at | 1 | mm | IEC 60695-2-12 |
Processing
| Injection Molding | Value | Unit | |
| Drying Temperature | 110 - 120 | °C | |
| Drying Time | 4 - 6 | hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 260 - 285 | °C | |
| Nozzle Temperature | 265 - 275 | °C | |
| Front - Zone 3 Temperature | 260 - 280 | °C | |
| Middle - Zone 2 Temperature | 255 - 280 | °C | |
| Rear - Zone 1 Temperature | 240 - 260 | °C | |
| Hopper Temperature | 40 - 60 | °C | |
| Mold Temperature | 60 - 110 | °C | |
| Source GMD, last updated:03/23/2000 | |||
| THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. | |||
| PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR AVAILABILITY IN YOUR REGION | |||
| (1) Typical values only. Variations within normal tolerances are possible for various colors. All values are measured after at least 48 hours storage at 23°C/50% relative humidity. All properties, except the melt volume and melt flow rates, are measured on injection molded samples. All samples tested under ISO test standards are prepared according to ISO 294. |
|||
| (2) Only typical data for selection purposes. Not to be used for part or tool design. | |||
| (3) This rating is not intended to reflect hazards presented by this or any other material under actual fire conditions. | |||
| (4) Internal measurements according to UL standards. | |||
Other related products we recommend:
|
For more information please download the datasheet |
|
 |
|
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
SAMTION INTERNATIONAL LIMITED
Location
Room 803B, 8/F., West Coast International Building, 290-296 Un Chau Street, Cheung Sha Wan, Kowloon, Hong Kong
Contact Person
Justin