Property

MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 50 mm/min	56	MPa	ASTM D 638
Tensile Stress, brk, Type I, 50 mm/min	37	MPa	ASTM D 638
Tensile Stress, yld, Type I, 5 mm/min	51	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	34	MPa	ASTM D 638
Tensile Strain, yld, Type I, 50 mm/min	3	%	ASTM D 638
Tensile Strain, brk, Type I, 50 mm/min	9	%	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	2.8	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	10	%	ASTM D 638
Tensile Modulus, 50 mm/min	2670	MPa	ASTM D 638
Tensile Modulus, 5 mm/min	2650	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	77	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	2600	MPa	ASTM D 790
Hardness, Shore D	78	-	ASTM D 2240
Tensile Stress, yield, 5 mm/min	50	MPa	ISO 527
Tensile Stress, break, 5 mm/min	35	MPa	ISO 527
Tensile Stress, yield, 50 mm/min	56	MPa	ISO 527
Tensile Stress, break, 50 mm/min	39	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	2.8	%	ISO 527
Tensile Strain, break, 5 mm/min	10	%	ISO 527
Tensile Strain, yield, 50 mm/min	3	%	ISO 527
Tensile Strain, break, 50 mm/min	8	%	ISO 527
Tensile Modulus, 1 mm/min	2600	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	80	MPa	ISO 178
Flexural Modulus, 2 mm/min	2700	MPa	ISO 178
Hardness, H358/30	100	MPa	ISO 2039-1
Hardness, Rockwell L	87	-	ISO 2039-2
Pencil Hardness test, 1kgf	HB	-	ASTM D 3363
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	80	J/m	ASTM D 256
Izod Impact, notched, -30°C	60	J/m	ASTM D 256
Multiaxial Impact	10	J	ISO 6603
Instrumented Impact Total Energy, 23°C	25	J	ASTM D 3763
Izod Impact, notched 80104 +23°C	12	kJ/m²	ISO 180/1A
Izod Impact, notched 80104 -30°C	7	kJ/m²	ISO 180/1A
Charpy 23°C, V-notch Edgew 80104 sp=62mm	13	kJ/m²	ISO 179/1eA
Charpy -30°C, V-notch Edgew 80104 sp=62mm	8	kJ/m²	ISO 179/1eA
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	89	°C	ASTM D 1525
HDT, 1.82 MPa, 3.2mm, unannealed	83	°C	ASTM D 648
CTE, -40°C to 40°C, flow	8.7E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	8.5E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	8.7E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	8.5E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate A/50	98	°C	ISO 306
Vicat Softening Temp, Rate B/50	91	°C	ISO 306
Vicat Softening Temp, Rate B/120	92	°C	ISO 306
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	87	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	77	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.06	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.4 - 0.7	%	S-Plastics Method
Melt Flow Rate, 220°C/10.0 kgf	25	g/10 min	ASTM D 1238
Density	1.07	g/cm³	ISO 1183
Melt Volume Rate, MVR at 220°C/10.0 kg	25	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 260°C/5.0 kg	33	cm³/10 min	ISO 1133
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Compliant, 94HB Flame Class Rating (3)(4)	1.5	mm	UL 94 by GE
Source GMD, last updated:10/09/2007

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	75 - 85	°C
Drying Time	2 - 4	hrs
Drying Time (Cumulative)	8	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	220 - 250	°C
Nozzle Temperature	220 - 240	°C
Front - Zone 3 Temperature	230 - 250	°C
Middle - Zone 2 Temperature	220 - 240	°C
Rear - Zone 1 Temperature	210 - 230	°C
Mold Temperature	40 - 80	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	60	rpm
Shot to Cylinder Size	50 - 70	%
Vent Depth	0.038 - 0.051	mm
Source GMD, last updated:10/09/2007