S-Plastic Ultem 1285 Transparent Polyimide Blend ECO Conforming US FDA And EU Food Contact Compliant In Recognized Co

Name: S-Plastic Ultem 1285 Transparent Polyimide Blend ECO Conforming US FDA And EU Food Contact Compliant In Recognized Co
Brand: SAMTION INTERNATIONAL LIMITED

Price Negotiable

Price: *USD

MOQ: 100KG

Delivery Time: To be negotiated

Brand: S-Plastic Ultem

Product Description

S-Plastics Ultem 1285 resin is Transparent Polyimide blend. ECO Conforming. US FDA and EU Food Contact Compliant in recognized colors.

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	110	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	82	MPa	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	60	%	ASTM D 638
Tensile Modulus, 5 mm/min	3370	MPa	ASTM D 638
Flexural Stress, yld, 2.6 mm/min, 100 mm span	165	MPa	ASTM D 790
Flexural Modulus, 2.6 mm/min, 100 mm span	3370	MPa	ASTM D 790
IMPACT	Value	Unit	Standard
Izod Impact, notched, 23°C	26	J/m	ASTM D 256
Izod Impact, Reverse Notched, 3.2 mm	950	J/m	ASTM D 256
Instrumented Impact Total Energy, 23°C	40	J	ASTM D 3763
THERMAL	Value	Unit	Standard
Vicat Softening Temp, Rate B/50	181	°C	ASTM D 1525
HDT, 1.82 MPa, 6.4 mm, unannealed	165	°C	ASTM D 648
CTE, -40°C to 40°C, flow	4.86E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	4.86E-05	1/°C	ASTM E 831
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.29	-	ASTM D 792
Mold Shrinkage, flow, 3.2 mm	0.6 - 0.7	%	S-Plastics Method
Melt Flow Rate, 295°C/6.6 kgf	8.1	g/10 min	ASTM D 1238
Source GMD, last updated:01/12/2000

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	4 - 8	hrs
Drying Time (Cumulative)	24	hrs
Maximum Moisture Content	0.02	%
Melt Temperature	300 - 330	°C
Nozzle Temperature	300 - 330	°C
Front - Zone 3 Temperature	295 - 325	°C
Middle - Zone 2 Temperature	290 - 320	°C
Rear - Zone 1 Temperature	280 - 315	°C
Mold Temperature	95 - 150	°C
Back Pressure	0.7 - 1.4	MPa
Screw Speed	50 - 100	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm
Source GMD, last updated:01/12/2000