Ultem AUT200M S-Plastic Pei Resin Pellets Bulk Transparent Highflow Polyimide (Tg 217C)
Price:
*USD
MOQ:
100KG
Delivery Time:
To be negotiated
Brand:
S-Plastic Ultem
Product Description
S-Plastics Ultem AUT200M resin is Transparent high flow Polyimide (Tg 217C) with internal mold release.. Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 204C (S-Plastics IP method).
Property
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | S-Plastics Method |
| Tensile Stress, yield, 50 mm/min | 105 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 85 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 60 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3300 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 160 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3300 | MPa | ISO 178 |
| Hardness, H358/30 | 140 | MPa | ISO 2039-1 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| Thermal Conductivity | 0.24 | W/m-°C | ISO 8302 |
| CTE, 23°C to 150°C, flow | 5.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate A/50 | 215 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 211 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 212 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 195 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 190 | °C | ISO 75/Ae |
| Metallized Haze Onset | 204 | °C | S-Plastics Method |
| PHYSICAL | Value | Unit | Standard |
| Mold Shrinkage on Tensile Bar, flow (2) | 0.5 - 0.7 | % | S-Plastics Method |
| Density | 1.27 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/sat) | 1.25 | % | ISO 62 |
| Moisture Absorption (23°C / 50% RH) | 0.7 | % | ISO 62 |
| Melt Volume Rate, MVR at 340°C/5.0 kg | 13 | cm³/10 min | ISO 1133 |
| Source GMD, last updated:12/11/2008 | |||
Processing
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 150 | °C |
| Drying Time | 4 - 6 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 370 - 410 | °C |
| Nozzle Temperature | 350 - 405 | °C |
| Front - Zone 3 Temperature | 360 - 415 | °C |
| Middle - Zone 2 Temperature | 350 - 405 | °C |
| Rear - Zone 1 Temperature | 340 - 395 | °C |
| Hopper Temperature | 80 - 120 | °C |
| Mold Temperature | 140 - 180 | °C |
| Source GMD, last updated:12/11/2008 | ||
|
For more information please download the datasheet |
|
 |
|
|
Get The Latest Quotation
First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials
|
Similar Products
Get in Touch
Have questions about our products or want to discuss a custom order? Our team is ready to help you.
Company
SAMTION INTERNATIONAL LIMITED
Location
Room 803B, 8/F., West Coast International Building, 290-296 Un Chau Street, Cheung Sha Wan, Kowloon, Hong Kong
Contact Person
Justin