Ultem PEI Resin

S-Plastic Ultem STM1600 resin is a flexible copolymer designed for wire and cable applications. It offers a halogen free (according VDE 0472) flame retardant solution that also offers low smoke emission and toxicity. It is an amber colored transparent material that can be selfcolored and easily processed on conventional equipment. The material may also have a fit in flexible profiles or injection molded parts. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I,

S-Plastic Ultem SF2360 resin is High flow Ultem for thin wall application ​Property MECHANICAL Value Unit Standard Tensile Stress, brk, Type I, 5 mm/min 148 MPa ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 2 % ASTM D 638 Tensile Modulus, 5 mm/min 11950 MPa ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 212 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 9940 MPa ASTM D 790 Tensile Stress, break, 5 mm/min 152 MPa ISO 527 Tensile Strain, break, 5 mm/min 2 % ISO

S-Plastic Ultem SF2350 resin is High flow Ultem blends for thin wall application ​Property MECHANICAL Value Unit Standard Tensile Stress, brk, Type I, 5 mm/min 172 MPa ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 2.6 % ASTM D 638 Tensile Modulus, 5 mm/min 11600 MPa ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 222 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 9320 MPa ASTM D 790 Tensile Stress, break, 5 mm/min 171 MPa ISO 527 Tensile Strain, break, 5 mm

S-Plastic Ultem SF2250 resin is High flow Ultem for thin wall application ​Property MECHANICAL Value Unit Standard Tensile Stress, brk, Type I, 5 mm/min 162 MPa ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 3 % ASTM D 638 Tensile Modulus, 5 mm/min 8900 MPa ASTM D 638 Flexural Stress, yld, 1.3 mm/min, 50 mm span 197 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 7260 MPa ASTM D 790 Tensile Stress, break, 5 mm/min 157 MPa ISO 527 Tensile Strain, break, 5 mm/min 3 % ISO

S-Plastic Ultem MD137 resin is AKA DU242HF. PRELIMINARY DATA. PEI+PCE. Fire helmet, thermal imager. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 75 MPa ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 60 % ASTM D 638 Tensile Modulus, 5 mm/min 2410 MPa ASTM D 638 Flexural Stress, yld, 2.6 mm/min, 100 mm span 99 MPa ASTM D 790 Flexural Modulus, 2.6 mm/min, 100 mm span 2340 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 144 J/m

S-Plastic Ultem MD123 resin is General purpose PEI/PPC blend. Nonhalogenated FR. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 75 MPa ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 90 % ASTM D 638 Tensile Modulus, 5 mm/min 2410 MPa ASTM D 638 Flexural Stress, yld, 2.6 mm/min, 100 mm span 113 MPa ASTM D 790 Flexural Stress, brk, 2.6 mm/min, 100 mm span 114 MPa ASTM D 790 Flexural Modulus, 2.6 mm/min, 100 mm span 2520 MPa ASTM D 790 IMPACT Value

S-Plastic Ultem MD110 resin is LIMITED USE: PEI/PC blend. Sampling requires ATE or PM approval. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 96 MPa ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 90 % ASTM D 638 Tensile Modulus, 5 mm/min 3300 MPa ASTM D 638 Flexural Stress, yld, 2.6 mm/min, 100 mm span 144 MPa ASTM D 790 Flexural Modulus, 2.6 mm/min, 100 mm span 3300 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 48 J/m

S-Plastic Ultem 2240 resin ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, yield 129 MPa S-Plastic - Japan Method Tensile Strain, break 9 - 9 % S-Plastic - Japan Method Flexural Stress 164 MPa ASTM D 790 Flexural Modulus 6870 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 61 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 3.2 mm, unannealed 209 °C ASTM D 648 Source GMD, last updated:06/13/2000 Processing THESE PROPERTY

S-Plastic Ultem MD107A resin is PRELIMINARY: Easy flow, opaque only. FDA. Repeat food service applications. ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 110 MPa ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 64 % ASTM D 638 Tensile Modulus, 5 mm/min 3790 MPa ASTM D 638 Flexural Stress, yld, 2.6 mm/min, 100 mm span 172 MPa ASTM D 790 Flexural Modulus, 2.6 mm/min, 100 mm span 3720 MPa ASTM D 790 Hardness, Rockwell M 109 - ASTM D 785 IMPACT Value

S-Plastic Ultem JD8901 ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 150 MPa S-Plastic - Japan Method Tensile Strain, break 10 - 10 % S-Plastic - Japan Method Flexural Stress 192 MPa ASTM D 790 Flexural Modulus 7510 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 77 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 3.2 mm, unannealed 209 °C ASTM D 648 FLAME CHARACTERISTICS Value Unit Standard UL Recognized, 94V-0 Flame Class Rating (3) 1.5 m

S-Plastic Ultem JD7920 resin For more information please download the datasheet S-Plastic Ultem JD7920.pdf Get The Latest Quotation First-level distribution source in South China Reduce procurement costs, improve supply stability, Help you find the most suitable engineering plastic materials Click to consult and get the latest quotation within 24 hours!

S-Plastic Ultem JD7904 resin ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 84 MPa S-Plastic - Japan Method Tensile Strain, break 4 - 4 % S-Plastic - Japan Method Flexural Stress 127 MPa ASTM D 790 Flexural Modulus 3720 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 29 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 3.2 mm, unannealed 200 °C ASTM D 648 PHYSICAL Value Unit Standard Specific Gravity 1.31 - ASTM D 792 Mold Shrinkage, flow, 3.

S-Plastic Ultem JD7903 resin ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 106 MPa S-Plastic - Japan Method Tensile Strain, break 9 - 9 % S-Plastic - Japan Method Flexural Stress 114 MPa ASTM D 790 Flexural Modulus 5180 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 33 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 3.2 mm, unannealed 213 °C ASTM D 648 PHYSICAL Value Unit Standard Specific Gravity 1.38 - ASTM D 792 Mold Shrinkage, flow, 3

S-Plastic Ultem JD7902 resin ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 127 MPa S-Plastic - Japan Method Tensile Strain, break 5 - 5 % S-Plastic - Japan Method Flexural Stress 186 MPa ASTM D 790 Flexural Modulus 5880 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 49 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 3.2 mm, unannealed 210 °C ASTM D 648 CTE, -30°C to 30°C 3.5E-05 - 3.5E-05 1/°C TMA PHYSICAL Value Unit Standard Specific

S-Plastic Ultem JD7410 resin ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 149 MPa S-Plastic - Japan Method Tensile Strain, break 8 - 8 % S-Plastic - Japan Method Flexural Stress 225 MPa ASTM D 790 Flexural Modulus 15200 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 49 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 3.2 mm, unannealed 212 °C ASTM D 648 CTE, -30°C to 30°C 1.5E-05 - 2.5E-05 1/°C TMA PHYSICAL Value Unit Standard Specific

S-Plastic Ultem JD7201 resin ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 204 MPa S-Plastic - Japan Method Tensile Strain, break 6 - 6 % S-Plastic - Japan Method Flexural Stress 255 MPa ASTM D 790 Flexural Modulus 13430 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 69 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 3.2 mm, unannealed 211 °C ASTM D 648 PHYSICAL Value Unit Standard Specific Gravity 1.34 - ASTM D 792 Water Absorption, 24

S-Plastic Ultem JD7101 resin ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 127 MPa S-Plastic - Japan Method Tensile Strain, break 6 - 6 % S-Plastic - Japan Method Flexural Stress 186 MPa ASTM D 790 Flexural Modulus 5090 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 44 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 3.2 mm, unannealed 208 °C ASTM D 648 PHYSICAL Value Unit Standard Specific Gravity 1.3 - ASTM D 792 Mold Shrinkage, flow, 3.

S-Plastic Ultem JD4912 resin ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 137 MPa S-Plastic - Japan Method Tensile Strain, break 3 - 3 % S-Plastic - Japan Method Flexural Stress 156 MPa ASTM D 790 Flexural Modulus 7360 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 34 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 3.2 mm, unannealed 211 °C ASTM D 648 CTE, -30°C to 30°C 2.E-05 - 2.E-05 1/°C TMA PHYSICAL Value Unit Standard Specific

S-Plastic Ultem JD4901 resin ​Property MECHANICAL Value Unit Standard Tensile Stress, yield 125 MPa S-Plastic - Japan Method Tensile Strain, break 3 - 3 % S-Plastic - Japan Method Flexural Stress 190 MPa ASTM D 790 Flexural Modulus 6470 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, notched, 23°C 78 J/m ASTM D 256 THERMAL Value Unit Standard HDT, 0.45 MPa, 3.2 mm, unannealed 213 °C ASTM D 648 PHYSICAL Value Unit Standard Specific Gravity 1.48 - ASTM D 792 Water Absorption, 24

S-Plastic Ultem FULC20 resin is Blowing agent in an ULTEM resin carrier, not a stand-alone material. See processing data for very basic guidelines. Processing Structural Foam Molding Value Unit Drying Time (Blowing Agent) 7 - 12 hrs Drying Temperature (Blowing Agent) 120 °C Concentration Range (Blowing Agent) 2 - 3 % Recommended Concentration (Blowing Agent) 2 % For more information please download the datasheet S-Plastic Ultem FULC20.pdf Get The Latest Quotation First-level