S-Plastic Thermocomp

S-Plastic Thermocomp MF006AL resin is a compound based on Polypropylene resin containing Glass Fiber. Characteristics of this grade are: Low ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 46 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 35 MPa ASTM D 638 Tensile Strain, yld, Type I, 5 mm/min 0.9 % ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 0.9 % ASTM D 638 Tensile Modulus, 50 mm/min 8240 MPa ASTM D 638 Flexural Stress, yld, 1.3 mm/min,

S-Plastic Thermocomp MF006A resin is a compound based on Polypropylene resin containing Glass Fiber. ​PropertyMECHANICALValueUnitStandardTensile Stress, yield, 50 mm/min81MPaISO 527Tensile Strain, yield, 50 mm/min1.9%ISO 527Tensile Modulus, 1 mm/min6500MPaISO 527Flexural Stress, yield, 2 mm/min102MPaISO 178Flexural Modulus, 2 mm/min6200MPaISO 178IMPACTValueUnitStandardIzod Impact, unnotched 80*10*4 +23°C20kJ/m²ISO 180/1UIzod Impact, notched 80*10*4 +23°C6kJ/m²ISO 180/1ATHERMALVal

S-Plastic Thermocomp MF0069S resin is a compound based on Polypropylene resin containing Glass Fiber, Flame Retardant. Added features of this material include: Chemically Coupled, Flame Retardant, Heat Stabilized. ​Property MECHANICAL Value Unit Standard Tensile Stress, break 71 MPa ASTM D 638 Tensile Strain, break 1.8 % ASTM D 638 Tensile Modulus, 50 mm/min 9300 MPa ASTM D 638 Flexural Stress 117 MPa ASTM D 790 Flexural Modulus 8120 MPa ASTM D 790 IMPACT Value Unit Standard Izod

S-Plastic Thermocomp MF004S resin is a compound based on Polypropylene resin containing Glass Fiber. Added features of this materialinclude: Chemically Coupled.​PropertyMECHANICALValueUnitStandardTensile Stress, break66MPaASTM D 638Tensile Strain, break3.1%ASTM D 638Flexural Stress106MPaASTM D 790Flexural Modulus4130MPaASTM D 790IMPACTValueUnitStandardIzod Impact, unnotched, 23°C534J/mASTM D 4812Izod Impact, notched, 23°C42J/mASTM D 256THERMALValueUnitStandardHDT, 1.82 MPa, 3.2mm

S-Plastic Thermocomp RC003 resin is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include: ​Property MECHANICAL Value Unit Standard Tensile Stress, break 201 MPa ASTM D 638 Tensile Strain, break 2.6 % ASTM D 638 Tensile Modulus, 50 mm/min 11720 MPa ASTM D 638 Flexural Stress 302 MPa ASTM D 790 Flexural Modulus 11260 MPa ASTM D 790 Tensile Stress, break 180 MPa ISO 527 Tensile Strain, break 2.4 % ISO 527 Tensile Modulus, 1 mm/min 11550

S-Plastic Thermocomp MF004AS resin is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: Heat Stabilized. ​Property MECHANICAL Value Unit Standard Tensile Stress, break 63 MPa ASTM D 638 Tensile Strain, break 2.3 % ASTM D 638 Tensile Modulus, 50 mm/min 4550 MPa ASTM D 638 Flexural Stress 92 MPa ASTM D 790 Flexural Modulus 4340 MPa ASTM D 790 Tensile Stress, break 65 MPa ISO 527 Tensile Strain, break 2.2 % ISO 527 Tensile

S-Plastic Thermocomp MF0044E resin is a compound based on Polypropylene resin containing Glass Fiber, Flame Retardant. Added features include: Non-Halogen Flame Retardant, Easy Molding. ​Property MECHANICAL Value Unit Standard Tensile Stress, yield, 5 mm/min 60 MPa ISO 527 Tensile Strain, break, 5 mm/min 3.9 % ISO 527 Flexural Stress, yield, 2 mm/min 80 MPa ISO 178 Flexural Modulus, 2 mm/min 4600 MPa ISO 178 IMPACT Value Unit Standard Izod Impact, unnotched 80*10*4 +23°C 30 kJ/m²

S-Plastic Thermocomp RB00A resin is 50% glass beads filled Polyamide 66 injection moulding resin. ​Property MECHANICAL Value Unit Standard Tensile Stress, break, 5 mm/min 85 MPa ISO 527 Tensile Strain, break, 5 mm/min 2.5 % ISO 527 Tensile Modulus, 1 mm/min 6200 MPa ISO 527 Flexural Stress, break, 2 mm/min 140 MPa ISO 178 Flexural Modulus, 2 mm/min 6000 MPa ISO 178 IMPACT Value Unit Standard Izod Impact, notched 80*10*4 +23°C 5 kJ/m² ISO 180/1A Izod Impact, notched 80*10*4 -20°C

S-Plastic Thermocomp 9H0600A resin is a compound based on XXXX resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break 0 MPa ASTM D 638 Tensile Strain, break 750 % ASTM D 638 Source GMD, last updated:02/27/2007 Processing THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR

S-Plastic Thermocomp RB008 resin is a compound based on Nylon 66 resin containing Glass Bead. ​Property MECHANICAL Value Unit Standard Tensile Stress, break 55 MPa ASTM D 638 Tensile Strain, break 3.3 % ASTM D 638 Tensile Modulus, 50 mm/min 5100 MPa ASTM D 638 Flexural Stress 102 MPa ASTM D 790 Flexural Modulus 3780 MPa ASTM D 790 Tensile Stress, break 58 MPa ISO 527 Tensile Strain, break 2.7 % ISO 527 Tensile Modulus, 1 mm/min 5430 MPa ISO 527 Flexural Stress 103 MPa ISO 178

S-Plastic Thermocomp MF003SU resin is a compound based on polypropylene resin containing Glass Fiber. Added features include : Heat ​Property MECHANICAL Value Unit Standard Tensile Stress, break, 5 mm/min 59 MPa ISO 527 Tensile Strain, break, 5 mm/min 3.2 % ISO 527 Tensile Modulus, 1 mm/min 3900 MPa ISO 527 Flexural Stress, yield, 2 mm/min 80 MPa ISO 178 Flexural Stress, break, 2 mm/min 45 MPa ISO 178 Flexural Strain, break, 2 mm/min 5.8 % ISO 178 Flexural Modulus, 2 mm/min 3500

S-Plastic Thermocomp MF003AS resin is PP, Glass Fiber, Heat Stabilized, ​Property MECHANICAL Value Unit Standard Tensile Stress, yld, Type I, 5 mm/min 29 MPa ASTM D 638 Tensile Stress, brk, Type I, 5 mm/min 59 MPa ASTM D 638 Tensile Strain, brk, Type I, 5 mm/min 1.5 % ASTM D 638 Tensile Modulus, 50 mm/min 8610 MPa ASTM D 638 Flexural Stress, brk, 1.3 mm/min, 50 mm span 57 MPa ASTM D 790 Flexural Modulus, 1.3 mm/min, 50 mm span 1780 MPa ASTM D 790 Tensile Stress, yield, 5 mm/min

S-Plastic Thermocomp 9H0300C resin is a compound based on XXXX resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break 1 MPa ASTM D 638 Tensile Strain, break 670 % ASTM D 638 Source GMD, last updated:02/27/2007 Processing THESE PROPERTY VALUES ARE NOT INTENDED FOR SPECIFICATION PURPOSES. PLEASE CHECK WITH YOUR (LOCAL SALES OFFICE) FOR

S-Plastic Thermocomp MF002S resin is a compound based on Polypropylene resin containing Glass Fiber. Added features of this materialinclude: Chemically Coupled, Heat Stabilized. ​PropertyMECHANICALValueUnitStandardTensile Stress, break51MPaASTM D 638Tensile Strain, break3.7%ASTM D 638Tensile Modulus, 50 mm/min3578370MPaASTM D 638Flexural Stress75MPaASTM D 790Flexural Modulus2868210MPaASTM D 790IMPACTValueUnitStandardIzod Impact, unnotched, 23°C517J/mASTM D 4812Izod Impact,

S-Plastic Thermocomp 5C004 resin is a compound based on Polyvinylidene Fluoride resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. ​Property TYPICAL PROPERTIES (1) MECHANICAL Value Unit Standard Tensile Stress, break 84 MPa ASTM D 638 Tensile Strain, break 0.7 % ASTM D 638 Tensile Modulus, 50 mm/min 16440 MPa ASTM D 638 Flexural Stress 137 MPa ASTM D 790 Flexural Modulus 13930 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact,

S-Plastic Thermocomp RB006ERP resin is a compound based on PA 66. Added features include: low density. ​PropertyMECHANICALValueUnitStandardTensile Stress, break, 5 mm/min74MPaISO 527Tensile Strain, break, 5 mm/min2.1%ISO 527Tensile Modulus, 1 mm/min4000MPaISO 527Flexural Stress, yield, 2 mm/min135MPaISO 178Flexural Modulus, 2 mm/min4500MPaISO 178IMPACTValueUnitStandardIzod Impact, unnotched 80*10*4 +23°C13kJ/m²ISO 180/1UIzod Impact, notched 80*10*4 +23°C2kJ/m²ISO 180/1APHYSICALVa

S-Plastic Thermocomp MF002AS resin is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: Heat Stabilized. ​Property MECHANICAL Value Unit Standard Tensile Stress, break 45 MPa ASTM D 638 Tensile Strain, break 3.7 % ASTM D 638 Tensile Modulus, 50 mm/min 3240 MPa ASTM D 638 Flexural Stress 68 MPa ASTM D 790 Flexural Modulus 2840 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, unnotched, 23°C 389 J/m ASTM D 4812 Izod

S-Plastic Thermocomp MF001AS resin is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: Heat Stabilized. ​Property MECHANICAL Value Unit Standard Tensile Stress, break 39 MPa ASTM D 638 Tensile Strain, break 4.9 % ASTM D 638 Tensile Modulus, 50 mm/min 2280 MPa ASTM D 638 Flexural Stress 55 MPa ASTM D 790 Flexural Modulus 2160 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, unnotched, 23°C 423 J/m ASTM D 4812 Izod

S-Plastic Thermocomp RB006 resin is a compound based on Nylon 66 resin containing Glass Bead. ​Property MECHANICAL Value Unit Standard Tensile Stress, break 66 MPa ASTM D 638 Tensile Strain, break 3 % ASTM D 638 Tensile Modulus, 50 mm/min 4320 MPa ASTM D 638 Flexural Stress 124 MPa ASTM D 790 Flexural Modulus 4690 MPa ASTM D 790 IMPACT Value Unit Standard Izod Impact, unnotched, 23°C 320 J/m ASTM D 4812 Izod Impact, notched, 23°C 32 J/m ASTM D 256 THERMAL Value Unit Standard HDT,

S-Plastic Thermocomp MCR13S resin is a compound based on Polypropylene resin containing Carbon Fiber, Barium Sulfate. Added featuresinclude: Heat Stabilized.​PropertyMECHANICALValueUnitStandardTensile Stress, yield, 5 mm/min48MPaISO 527Tensile Strain, break, 5 mm/min1%ISO 527Flexural Stress, yield, 2 mm/min65MPaISO 178Flexural Modulus, 2 mm/min6300MPaISO 178IMPACTValueUnitStandardIzod Impact, unnotched 80*10*4 +23°C20kJ/m²ISO 180/1UTHERMALValueUnitStandardHDT/Af, 1.8 MPa Flatw 80