China 2.35mm Aluminum Alloy Sheet Plate 5052 For Instrument Panel for sale

2.35mm Aluminum Alloy Sheet Plate 5052 For Instrument Panel

Name: 2.35mm Aluminum Alloy Sheet Plate 5052 For Instrument Panel
Brand: Shanghai Moopec Ltd

Price Negotiable

Price: $3.36/Kilograms >=500 Kilograms

MOQ: 500 Kilograms

Delivery Time: Negotiable

Brand: BAO STEEL

Product Description

2.35mm Aluminum Alloy Sheet Plate 5052 For Instrument Panel

Application:	Port	Width:	980~2450mm
Alloy Or Not:	Is Alloy	Grade:	5000 Series
Surface Treatment:	Coated	Temper:	O - H112/T351 - T851/T3-T5
Tolerance:	±5%	Processing Service:	Welding, Punching, Cutting
Product Name:	Aluminum Alloy Plate	Thickness:	1.0~60mm
Alloy:	1050/1060/1100/3003/3004/5005/5052/5083/3005/8011	Material:	Aluminum Material
Standard:	ASTM AISI JIS DIN GB	Surface:	Smooth
Shape:	Coil.sheet	Type:	Coilplate
PAYMENT TERM:	L/C T/T(30% Deposit)	PRICE TERM:	CIF CFR FOB Ex-Work
Port:	Shanghai Port , China
High Light:	2.35mm Aluminum Alloy Sheet , Aluminum Alloy Sheet 5052 , 5052 aluminum plate

aluminium alloy

The 5005 aluminum alloy is similar to the 3003 alloy in that it has medium strength and good corrosion resistance. The 5005 aluminum alloy is used as a conductor, cooker, instrument panel, shell and architectural decoration. The anodic oxide film is brighter than the oxide film on alloy 3003 and is consistent with the hue of alloy 6063.

The 5005 aluminum alloy is similar to the 3003 alloy in that it has medium strength and good corrosion resistance. The 5005 aluminum alloy is used as a conductor, cooker, instrument panel, shell and architectural decoration. The anodic oxide film is brighter than the oxide film on alloy 3003 and is consistent with the hue of alloy 6063

Component(Wt%)
Si(≤)	Fe(≤)	Cu(≤)	Mn(≤)	Zn(≤)	cr(≤)	Mg(≤)	Al(≤)
0.30	0.00~0.70	0.20	0.20	0.25	0.1	0.50~1.1	All the rest

Mechanical properties	Yield strength σ(Mpa)	155~195
	Tensile strength σ 0.2 (Mpa)	≥125
	Elongation δ 5(%)	≥2

	Temperature	holding time	cooling mode
Homogenization annealing	460~475℃	12~14h	Air cooling
Rapid annealing	350~410℃	30~120min	Air or water cooling
High temperature annealing	350~420℃	10~30/2~10min	Air cooling
Low temperature annealing	250~300℃	1~2h	Air cooling