Automotive Steel Sheet

GMW2M-ST-S-HR3-UNCOATED/HD40G40G/HD50G50G/HD60G60G-U Chemical Composition(％ by mass) Element CR1,HR0 CR2,CR3,HR1,HR2,HR3 CR4 CR5 Carbon 0.13max 0.10max 0.08max 0.02max Manganese 0.60max 0.50max 0.40max 0.25max Phosphorus 0.035max 0.025max 0.025max 0.020max Sulfur 0.035max 0.020max 0.020max 0.020max Aluminum N/A 0.015min 0.015min 0.015min Nitrogen 0.008max N/A N/A N/A Mechanical Propeerties Property Unit Designation GMW2M-ST-S CR1 CR2 CR3 CR4 CR5 Yield Strength MPa 140-280 140

High-strength steel HC420/780DPD+Z hot-dip galvanized steel for automotive steel material With dual-phase steel, pure zinc coating, zinc-iron alloy coating, HC420/780DPD+Z hot-dip galvanized steel sheet for electrical appliances has strong coating adhesion, strong erosion resistance, accurate control of the thickness of the galvanized layer, high dimensional accuracy, flat profile and good Mechanical, processing and welding performance. They can be used to manufacture outer

GMW2M-ST-S-CR3 UNCOATED/ HD50G50G/HD60G60G-U Item # Steel Type GMW2M-ST-S-CR1 Commercial Quality GMW2M-ST-S-CR2 Forming Steel GMW2M-ST-S-CR3 Drawing Quality GMW2M-ST-S-CR4 Deep Drawing Quality GMW2M-ST-S-CR5 Extra Deep Drawing Quality GMW2M-ST-S CR3 Chemical Compositions Element Min Max C - 0.1 Mn - 0.5 P - 0.025 S - 0.02 Al 0.015 - GMW2M-ST-S CR3 Mechanical Properties Yield(MPa) Tensile(MPa) Elongation 140~210 270~350 38 (≥)

SPCE steels are deep drawing quality cold rolled steels, which are consumed for drawing applications. This material is valid for drawing operation where the depth of the drawn part exceeds its diameter. Grade Q/BQB EN GMW ASTM GB PSA DIN DC04/SPCE/BUSD DC04 CR3 CS Type A,B DC04 ES ST14 SPCE Chemical Composition( %) Standard Element Material/Grade C Mn Si P S JIS G 3141 SPCE 0.08 0.45 -- 0.03 0.03 SPCE Mechanical Properties( MPa-Min) Tensile Strength Yield Strength Elongation

High-strength steel HC550/980DPD+Z hot-dip galvanized steel for automotive steel material Product characteristic: No yield extension, five times of room temperature aging, low yield strength ratio, high machining hardening index, high bake hardening value. main application: DP series high-strength steel is currently the first choice for structural parts. It is used for structural parts, reinforcements and anti-collision parts, such as car bottom beams, guide rails, anti

High-strength steel HC420LAD+Z hot-dip galvanized steel for automotive steel material With high-strength low-alloy steel, pure zinc coating, zinc-iron alloy coating, HC420LAD+Z hot-dip galvanized steel sheet for household appliances has strong coating adhesion, strong erosion resistance, accurate control of the thickness of the galvanized layer, high dimensional accuracy, flat profiles, and Good mechanical, processing and welding performance. They can be used to manufacture

S355MC is a hot-rolled high-strength low-alloy steel. It combines high strength, excellent forming ability and consistent quality. It replaces traditional construction steel and is suitable for applications where high strength is essential. It is ideal for load-bearing and lifting applications, including earth-moving equipment and agricultural machinery. It is also a popular choice for stamping parts such as car seat parts, radiators and fuel systems. The high yield strength

Duplex and multiphase steels 1. Bumper DP1180 2. Front cross member DP780 3. Middle channel DP450 4. Side beam DP980/CP1000 5. B-pillar reinforcement DP600 Illustrate: Due to their special microstructure (high-hardness martensite and bainite phases dispersed in a softer ferrite matrix), duplex and multiphase steels combine strength and formability perfectly. These grades have high strain hardenability, good strain redistribution and formability. In addition, the mechanical

Hot stamping steel 1. Bumper 2. A-pillar 3. Door anti-collision 4. Edge beam 5. B-pillar reinforcement 6. Front longitudinal member Illustrate: It is a hot forming steel grade suitable for automotive structural parts and safety parts. The mechanical strength of the finished part is very high, which can reduce the weight of the car by 30% to 50% compared to traditional cold-formed steel grades. It is suitable for parts that need to absorb energy in the event of a collision.

Automotive IFHS (Interstitial Free High Strength Steel) 1. Hair hood 220IFHS Illustrate: The design of this type of steel is based on its specific interstitial-free steel (IF) metallurgical properties, providing an excellent combination of formability and mechanical strength. Such steels are strengthened by adding manganese, silicon, and phosphorus to ferrite in solid solution. This type of steel is particularly suitable for products requiring high mechanical strength, such

BH (Bake Hardened Steel) 1. Hair cover 180BH 2. Door 260BH The composition and processing of these steels are specially designed to ensure a significant increase in yield strength during low temperature heat treatment, especially during paint baking. Thanks to this, VAMA bake hardening steels are able to achieve higher strengths while maintaining good forming results. By using the "bake hardening" (BH) process, the yield strength can usually be increased by more than 35Mpa.

HSLA (cold formed high strength low alloy steel) 1. Energy absorbing box HSLA300 2. Rear longitudinal beam HSLA300 Illustrate: The high-strength low-alloy (HSLA) series of steels are strengthened through a combination of precipitation and grain refinement mechanisms to achieve low-alloy high strength. Since this series of steel grades neither cause softening of the weld zone nor coarsening of the grains, the weldability is enhanced and the range of coating options is expanded

Automotive Low Carbon Steel (High Formability Steel) 1. Rear floor DC04 2. Wheel cover DC06 Illustrate: These products are unalloyed low carbon steels suitable for deep drawing/extra deep drawing applications, widely used on visible components and structural parts in the automotive industry. Its low scattering in mechanical properties ensures efficient production of the stamping process. Application: These steels are used for deep drawing/extra deep drawing of visible and

High-strength steel cold rolled hot dip galvanized steel H300LAD+Z for automotive steel material H300LAD+Z hot-dip galvanized sheet (coil) has the characteristics of strong coating adhesion, strong erosion resistance, accurate control of the thickness of the galvanized layer, high dimensional accuracy, flat profile, good mechanical, processing, and welding performance. They can be used to manufacture automotive interior and exterior panels, structural parts and reinforcements

GMW2M-ST-S-HR1/GMW2M-ST-S-HR1-HD60G60G-U Chemical Composition(％ by mass) Element CR1,HR0 CR2,CR3,HR1,HR2,HR3 CR4 CR5 Carbon 0.13max 0.10max 0.08max 0.02max Manganese 0.60max 0.50max 0.40max 0.25max Phosphorus 0.035max 0.025max 0.025max 0.020max Sulfur 0.035max 0.020max 0.020max 0.020max Aluminum N/A 0.015min 0.015min 0.015min Nitrogen 0.008max N/A N/A N/A Mechanical Propeerties Property Unit Designation GMW2M-ST-S CR1 CR2 CR3 CR4 CR5 Yield Strength MPa 140-280 140-240 140-210

GMW2M-ST-S-HR2-UNCOATED/HD40G40G/HD50G50G/HD60G60G-U Chemical Composition(％ by mass) Element CR1,HR0 CR2,CR3,HR1,HR2,HR3 CR4 CR5 Carbon 0.13max 0.10max 0.08max 0.02max Manganese 0.60max 0.50max 0.40max 0.25max Phosphorus 0.035max 0.025max 0.025max 0.020max Sulfur 0.035max 0.020max 0.020max 0.020max Aluminum N/A 0.015min 0.015min 0.015min Nitrogen 0.008max N/A N/A N/A Mechanical Propeerties Property Unit Designation GMW2M-ST-S CR1 CR2 CR3 CR4 CR5 Yield Strength MPa 140-280 140

GMW2M-ST-S-CR2-UNCOATED/ HD40G40G/HD50G50G/HD60G60G-U Item # Steel Type GMW2M-ST-S-CR1 Commercial Quality GMW2M-ST-S-CR2 Forming Steel GMW2M-ST-S-CR3 Drawing Quality GMW2M-ST-S-CR4 Deep Drawing Quality GMW2M-ST-S-CR5 Extra Deep Drawing Quality Chemical Composition(％ by mass) Element CR1,HR0 CR2,CR3,HR1,HR2,HR3 CR4 CR5 Carbon 0.13max 0.10max 0.08max 0.02max Manganese 0.60max 0.50max 0.40max 0.25max Phosphorus 0.035max 0.025max 0.025max 0.020max Sulfur 0.035max 0.020max 0

GMW2M-ST-S-CR4-UNCOATED/ HD40G40G/HD50G50G/HD60G60G/HD70G70G-U Item # Steel Type GMW2M-ST-S-CR1 Commercial Quality GMW2M-ST-S-CR2 Forming Steel GMW2M-ST-S-CR3 Drawing Quality GMW2M-ST-S-CR4 Deep Drawing Quality GMW2M-ST-S-CR5 Extra Deep Drawing Quality Chemical Composition(％ by mass) Element CR1,HR0 CR2,CR3,HR1,HR2,HR3 CR4 CR5 Carbon 0.13max 0.10max 0.08max 0.02max Manganese 0.60max 0.50max 0.40max 0.25max Phosphorus 0.035max 0.025max 0.025max 0.020max Sulfur 0.035max 0

GMW2M-ST-S-CR5-UNCOATED/ HD40G40G/HD50G50G/HD60G60G/HD70G70G-U Item # Steel Type GMW2M-ST-S-CR1 Commercial Quality GMW2M-ST-S-CR2 Forming Steel GMW2M-ST-S-CR3 Drawing Quality GMW2M-ST-S-CR4 Deep Drawing Quality GMW2M-ST-S-CR5 Extra Deep Drawing Quality Chemical Composition(％ by mass) Element CR1,HR0 CR2,CR3,HR1,HR2,HR3 CR4 CR5 Carbon 0.13max 0.10max 0.08max 0.02max Manganese 0.60max 0.50max 0.40max 0.25max Phosphorus 0.035max 0.025max 0.025max 0.020max Sulfur 0.035max 0

Pickled and oiled PO SAPH440 steel coil SAPH370 SAPH400 SAPH440 automotive structural steel sheet What is SAPH440 Steel? SAPH440 steel is structural hot-rolled steel in the form of plates, sheets & strips for automobile structural applications. SAPH440 is a material grade and designation defined in JIS G3113 standard. SAPH440 steel coil chemical composition: Grade P S SAPH440 ≤0.040 ≤0.040 SAPH440 steel coil mechanical properties: Grade Tensile Strength N/mm² Yield Strength