ISO 45001 Functional Latent Curing Agent Additive For Decorative CT0320
Decorative Paper Functional Additives Latent Curing Agent FENTENGCT0320
| Color | Colorless or light yellow |
| Density | 1.2-1.3 g/ml |
| pH | 3.0-4.0 |
| Product Group | Catalysts |
| Package | 200kg round plastic drum or 1000L square plastic drum |
| State | liquid |
|
Type
|
Salt Mixture |
| Be used in | Melamine formaldehyde(MF) resin |
| Bio-based Content | 0%-30% |
| Effect:wood processing | Seond stage coater latent |
| Market | Wood precessing |
| Solubilit in water | soluble |
| Boiling point | About 90-100c |
| Volatile component(%volume) | N/A |
| Relative vapor density (air＝1) | N/A |
| Heat of combustion(ºC): | N/A |
| Lower explosive limit% | Not applicable |
Description:
1.CT0320 is a MF curing agent with wide resin applicability and good latency (latency is no curing at low temperature, fast curing at high temperature)
2.In the low-formaldehyde formula and rapid pressing process formula, CT0320 can provide better latency.
3.Stronger latency, no curing at lower temperature, rapid curing at high temperature. Using this product can make the resin flow better under pressure and cure more uniformly.
3. With the plasticizer RP107, it can improve the film-forming properties of the resin and improve the pollution resistance. .
4.Improve the clarity of decorative wood grain
5.Extend the active period of the MF resin stored at room temperature.
Applications:
1.Add about 0.1-0.4% of MF to the liquid resin
2.The degree of reaction depends on the PH value and reactivity of the resin. The boiling water curing time of the resin ranges from 4-8 minutes.
3.The curing agent should be added last after adding other kinds of additives
How to use additives
1.Urea glue curing agent will be added to the UF resin impregnated in the front stage of furniture impregnated paper production, and the amount of addition is subject to the detection of curing time. Then add penetrant, the addition amount is generally 0.2%. Anti-sticking agent can also be added, the addition amount is 0.3%.
2.In the coating section, MF resin is added with triamine glue curing agent, and the amount of addition is subject to the detection of curing time. It is also necessary to add a release agent, the addition amount is 0.2%. In addition, 0.1%-0.2% dust remover can be added according to the glue usage. If UF is used for the bottom coating, it is not necessary to add a release agent, but add 0.3% anti-sticking agent .
Notices:
1.The storage period is one year, please use it as soon as possible.
2,When the temperature is too low, freezing or crystallization may occur, and the effect will not be affected after thawing, but after thawing, testing is required to ensure that the product performance is within the qualified range.