High Voltage Ceramic Disc Capacitor 4700pF 1KV Y5V P5mm For Power System

Price Negotiable

Price: Negotiable

MOQ: 10000pcs

Delivery Time: 12~15 working days

Brand: ETOPMAY

Product Description

High Voltage Ceramic Disc Capacitor 4700pF 1KV Y5V P5mm For Power System

Specification of Capacitor

TOPMAY Part No: TMCC02-472M1KVP5A
Rated Voltage:1000V
Capacitance: 4700Pf
Tolerance: +-20%
Material Type: Y5V (Temperature. Characteristic: +22%,-82%)
Blue Epoxy coating
Pitch:P=5mm(±1mm) Diameter:6mm ±1mm
Operating Temperature Range:–25℃～+105℃
Testing Using Condition: Temperature: 15~35℃ Humidity: 45%~ 75% Atmospheric pressure: 86~106Kpa

Capacitor Parameters:

No.	Item		Charateristics	Testing Method (GB 2693-2001 GB／T9322-88)
1	Outlook and Size		No visible damage and in accordance with the size requirements, see Table 2	Visual inspection and gage inspection
2	Marks		in accordance to No.7
3	Capacitance		Meet tolerance requirement	Testing temperature 25℃, Frequency 1±0.2KHz Voltage 1Vmax
4	Loss Tangent		Y5P(B)≤250×10^-4 BN≤50×10 Y5V(F)≤350×10^-4	Testing method is the same to that for capacitance
5	Insulation Resistance		RI＞4000MΩ	500VDC,charging time 60±5S
6	Withstand Voltage	Between terminal	Without failure	Add voltage 1.5U_R+500V to between lead terminals for DC voltage 2S,no arcing and breakdown, leakage current ＜50mA
		Coating	Without failure	The two leads are short circuited, the capacitance is placed in a steel ball with a diameter of 1mm, and the root is exposed for 2mm. Add 1500V DC voltage between the lead and the steel ball for 5S.
7	Temperature characteristics	Without adding voltage	Y5P(B),BN:±10％	Step	1	2	3	4	5	6	7
		Adding voltage	Y5P(B),BN:＋10％／－15％	Temp. ℃	20±2	-25±3	20±2	85±2	85±2	20±2	-25±2
				UR	/	/	/	/	Rated	Rated	Rated
8	Lead strength		No damage	Fix the capacitor and apply force. Apply force of 10N when the lead diameter is more than 0.5mm and 5N when the lead diameter is less than 0.5mm. Keep it for 10 ± 1s, and the lead out end bears secondary bending
9	Resistance to welding heat	Outlook	No damage	Soldering temperature 245±5℃, time 5±0.5S, The insertion depth is 2.5mm away from the porcelain body, and the insertion speed is 1s. Measure 24 ± 2h after the test
		ΔC/C	Y5P(B),BN≤±10％ Y5V(F)≤±20％
10	Vibration	Outlook	No damage	Frequency 10～500Hz, amplitude 0.75mm, time 6h, 2h in each direction, three directions.
		Capacitance	Meet tolerance requirement
11	Steady Damp Heat	Outlook	No damage, clear remark	Time 500＋２４ｈ－０ｈ, temperature 40±2℃, Humidity 90～95%,after testing,resume to room temperature a to Test after 24 hrs.
		ΔC/C	Y5P(B),BN≤±10％ Y5V(F)≤±30％
		Loss tangent	Y5P(B) ≤400×10^-4 BN≤150×10^-4 Y5V(F)≤700×10^-4
		Insulation Resistance	≥1000MΩor RI*CR≥25s which smaller
12	Durability	Outlook	No damage, clear remark	The temperature is 85 ± 2 ℃, the duration is 1000h, the test is completed with 1.5 times of rated voltage (DC), and the room temperature is restored to 24h ± 2H for measurement.
		ΔC/C	Y5P(B),BN, Y5V(F)≤30%
		Loss Tangent	Y5P(B)≤400×10^-4 BN≤150×10^-4 Y5V(F)≤700×10^-4
		Insulation Resistance	≥2000MΩ or Ri*CR≥25s which smaller
13	Lead solderability		Wet the solder at the lead out end and flow freely to show that the tin coating is good	After the capacitor lead is immersed in 25% alcohol rosin solution, it is immersed in soldering tin with melting temperature of 260 ± 5 ℃ for 2 ± 0.5s, and the immersion depth is 2 ~ 2.5mm away from the porcelain body

Dimension

Size Code	Specification	Size Code	Specification
F	5 +0.8-0.2	W2	0~1.5
Po	12.7±0.3	H	20 +1.5 -1.0
P	12.7±1.0	Ho	16 +1.0 -0.5
P1	3.85±0.7	Do	4±0.2
P2	6.35±1.0	△h	0±1.0
W1	9.0±0.5	T2	1.5max