Safety Ceramic Disc Capacitor X1 Y1 2.2nF 400VAC P10mm Y5V For Power Filter

Specifications

1. TOPMAY Part No: TMCC02-222M400VP10B
2. Safety Class: X1Y1
3. Capacitance: 2200pF
4. Rated Voltage:400 VAC
5. Material Type: Y5V (+-20%)
6. Pitch:P=10.0mm±0.5mm
7. Operating Temperature Range:–25℃～+85℃
8. Static Capacitance:When the temperature is below 25±2℃,the frequency is 1KHZ and the head voltage is in the scope of 1.0Vrms max.
9. Insulated Impedance:According the Ration Voltage is added more than 6000 MΩ for one minute.
10. Pressure: When the Ration Voltage is 5KVDC or 4000VAC , add the Ration Voltage for 1～5, there is no abnormity happened.
11. Temperature Characteristics:

B: Y5P E: Y5U F: Y5V

Dimensions (mm)

Standard and Test Method

Test Condition

Test must be in the standard condition( Temperature 15～30℃, Relative humidity 45～75%, air pressure 86～106Kpa)

Unless otherwise specified, capacitance must be under base conditions in case of doubt of measurement results and special requirements (Temperature 25±2℃, Relative humidity 60～70%, air pressure 86～106Kpa). Apply to X1Y1 and X1Y2.

No.

Item

Standard

Test Condition

1

Appearance and size

There is no obvious defect in appearance shape, the size is within the standard range

Capacitance must be visually checked for obvious defects. Dimensions are measured with vernier calipers.

2

Printing

Clear and could be recognized.

Visual Check.

3

Capacitance

Within the specified tolerance range

Capacitance and Dissipation factor must be tested under the temperature 20℃, and 11KHz, 1±0.1V

4

(D.F.) Dissipation Factor

≤200×10-4

5

(I.R.) Insulation Resistance

≥10000MΩ

Insulation resistance must be tested after charging 60±5 seconds under voltage 500±50V.

6

Dielectric strength

Between two terminals

There is no breakdown or arc.

(The charge and discharge current is not greater than 50mA) The capacitor is added voltage in the below table, after 60s, there is no damage, <Table 1> Item Tested Voltage X1Y2 AC2600V (r.m.s.) X1Y1 AC4000V (r.m.s.)

The body insulation

There is no breakdown or arc.

First, the terminals of the capacitor are twisted together, and then, as shown in the figure on the right, the metal foil is wrapped around the capacitor's body 3-4mm away from the terminal. Then, the capacitor is inserted into the container holding a metal ball with a diameter of 1mm. Finally, the AC voltage as shown in table 2 is applied for 60 seconds. <Table 2> Type Test Voltage X1Y2 AC1500V(r.m.s.) X1Y1 AC4000V(r.m.s.)

7

Temperature Characteristics

Item Capacitance change B(Y5P) ±10% E(Y5U) +22/-56% F(Y5V) +30/-80%   Temperature Range: -25 ～ +125℃

The capacitor must be tested under temperature as below Table 3 <Table 3> Process 1 2 3 4 Temperature (℃) 20 ±2 -25 ±3 20 ±2 85 ±2

8

Resistance to soldering heat

Appearance

No damage

The conductor of the capacitor must be immersed in the solder for 5 + / -0.5 seconds. Dip depth 2.5 mm from wire root. Soldering temperature: 250±5℃ 24±2hrs later, make testing.

Capacitance change rate

ΔC/C≤10%

9

Vibration resistance

Appearance No damage

Frequency 10~500Hz, total amplitude to 0.75mm, time 6hrs

10

Humidity

Appearance

No damage

The time was 500+24- 0h, the temperature was 40±2℃ and the temperature was 90 ~ 95%. After the test was completed, the temperature was restored to 24±2h at room temperature.

Capacitance change rate

ΔC/C≤15%

I.R. Insulation Resistance

≥3000MΩ

Loss Tangent

△tanδ≤80×10-4

11

Durability

Appearance

No damage

The temperature was 85±2℃, the duration was 1000h and the rated voltage was 1.7 times. After the test, the temperature was restored to 24±1h

Capacitance change rate

≤20%

I.R. Insulation Resistance

≥3000MΩ

Loss Tangent

△tanδ≤80×10-4

12

Lead Weldability

Wet lead solder, free flow to indicate good tin coating

After the capacitor leads are immersed in 25% alcohol rosin solution, they are immersed in solder with melting temperature of 235±5℃ and 2± 0.5s into the depth of 2 ~ 2.5mm away from the porcelain body.

13

Flame retardant test

Apply flame duration 30S, residual flame duration ≤10S.

Apply flame duration 30S, residual flame duration ≤10S.

14

Impulse test

The capacitor shall have no failure

Add the capacitor to the pulse voltage y1:8kvdc and y2:5kvdc, and make 24 pulses of the same polarity, at a time interval of not less than 10S

Our series of strong products of capacitors and resistors can be divided into below types:

★ Ceramic Disc Capacitor( low and high voltage, Y1/Y2 safety )

★ Multilayer Ceramic Capacitor( radial, axial and SMD )

★ Film Capacitor( Mylar, MKT, MKP, X2, CBB60, CBB61, CBB65, CL21-Box, CBB-BOX, CL20, CBB20, CBB81, etc. )

★ Aluminum Electrolytic Capacitor(SMD, Radial , Axial, Snap-in , Screw Terminal, etc. )

★ Tantalum Capacitor(SMD, Radial , Axial )

★ Super Capacitor( Coin Type, Cylindrical Type, Module Type)

★ Mica Capacitor

★ Trimmer Capacitor

★ SMD Resistors

★DIP TYPE Resistors( KNP, CF, MF, MOF, ect,)

★ Cement Resistors

★ Leadless Resistors( MLEF)

★Power Resistor

Any more details, kindly contact us freely!