6082 T6 T6511 Alloy Solid Aluminum Bar For Transportation Tools
Large Diameter 6082 Solid Aluminum Bar Aluminum Round Rod Bar
6082 Aluminum Bar Characteristics:
6082 is an alloy that can be strengthened by heat treatment. It belongs to 6000 series aluminum, which is a medium strength alloy with good formability, weldability, machinability and corrosion resistance. It can still maintain good operability after annealing.
Mainly used in mechanical structure. Including bar, plate, pipe.
The T6 state has high mechanical properties. Alloy 6082 is a commonly used alloy product in Europe and has high applications in the United States for processing raw materials, seamless aluminum tubes, structural and custom profiles.
The 0 and T4 states of alloy 6082 are suitable for bending and forming applications.
The T5 and T6 states are suitable for good machinability. Some specific processes require the use of chip separators or other special processes to help separate chips.
6082 alloy usually has good processing characteristics and anode reaction performance.
6082 Aluminum Bar Chemical Composition (%):
| Grade | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Al |
| 6082 | 0.7-1.3 | 0.5 | 0.1 | 0.40-1.0 | 0.6-1.2 | 0.25 | 0.2 | 0.1 | remaining |
6082 Aluminum Bar Mechanical Properties:
| Brand | Status | Diameter/mm |
Strength of Extension Rm/Mpa |
Yield Strength Rp0.2/Mpa |
Ductility/% | Bending Radius α | |||||
| A5.65 | A50mm | 180° | 90° | ||||||||
| Not smaller than | |||||||||||
| 6082 | O,H111 | ≤200 | ≤160 | ≤110 | 14 | 12 | — | — | |||
| T4 | ≤200 | 205 | 110 | 14 | 12 | — | — | ||||
| T6 | ≤20.0 | 295 | 250 | 8 | 6 | — | — | ||||
| >20-150 | 310 | 260 | 8 | — | — | — | |||||
| >150-200 | 280 | 240 | 6 | — | — | — | |||||
| >200-250 | 270 | 200 | 6 | — | — | — | |||||
Density: 2.85g/cm³
Hardness: O State:40HB; T4,T451 State:58HB; T6,T651 State:90HB
6082 T6 - Solution heat treated and artificially aged
6082 T4 - Solution heat treated and naturally aged to a substantially stable condition
6082 T651 - Solution heat treated, stress relieved by stretching then artificially aged
6082 T6511 - Solution heat-treated, stress-relieved by controlled stretching, and minor straightening is allowed after stretching to comply with standard tolerances then artificially aged.
6082 Aluminum Bar Applications:
6082 is widely used in aviation fixtures, towers, boats, trucks, pipes, and other building applications requiring, weldability strength and corrosion resistance. Such as: aircraft parts, camera lenses, couplers, ship accessories and hardware, decorative or various hardware, electronic accessories and joints, magnetic head, hinge head, hydraulic piston, brake piston, electrical accessories, valves and valve parts.