Superelastic Alloy

Phynox No Magnetic Corrosion Resistant Alloy with High Elasticity Phynox is an equal grades of Elgiloy(Registered Trad Mark of ESM). What makes Phynox an outstanding material for elastic parts: Excellent resistance to corrosion, stress corrosion cracking and hydrogen embtittlement
Could work in a wide range of temperatures, from -185°C to 450°C
Perfect passivity in contact with human tissues
so as to be employed in humen body Strength incresed by 10% by age hardening

R30003 Cold Drawn Wire ASTM F1058-08 for Surgical Implant Applications The alloy compostion covered by ASTM F1058-08 has be employed successfully in human implant applications in contact with soft tissue and bone for over a decade. So far there is no surgical implant material has ever been shown to be completely free of adverse reactions in the human body. But long-term clinical experience of the use of UNS R30003 and UNS R30008 has shown that an acceptable level of

ISO 5832-7 Forgeable and Cold-formed Cobaltchromium-nickel-molybdenum-iron Alloy A-ONE ALLOY supplys R30003 strip per Implants for surgery -Metallic materials - Part 7: Forgeable and cold-formed cobaltchromium-nickel-molybdenum-iron alloy Chemical composition ISO 5832-7 Element Element compositional limits, % (m/m) Cobalt Chromium Nickel Molybdenum Manganese Silicon Carbon Phosphorus Sulfur Beryllium Iron 39 to 42 18,5 to 21,5 14 to 18 6,5 to 8,0 1,0 to 2,5 1 max. 0,15 max. 0

3J21 Elastic Alloy Cold Drawn Wire Diameter 0.20-2.0mm for Spring A-ONE ALLOY supplies 3J21 alloy for elastic components in shape of hot rolled strip, cold rolled strip, cold drawn wire, hot forged round bar and forging pieces. We are one of the few manufacturers in China who are able to supply 3J21 in all shapes. And because of regular orders from customers, we keep ingot of 3J21 in stock to make fast delivery. Meanwhile, it makes it possible to accept a MOQ of 20kg for

3J21 Superelastic Alloy for Elastic Component Strip Thickness 0.05-2.50mm A-ONE ALLOY supplies 3J21 alloy for elastic components. Successful project: Spring energized seal-Italian customer The customer used Phynox strip from France in the past. After 6 months' strict test in the lab, our 3J21 strip is commented as excellent in performance. Characters Combination of high strength, ductility and good mechanical properties at ambient temperatures Excellent fatigue life Excellent

ASTM F1058 R30003 Round Bar Non-magnetic Cobalt-Chromium-Nickel-Molybdenum Alloy Xunshi keeps in stock of R30003 raw material and make it possible to deliver R30003 round bar within 4 weeks. UNS R30003 (Co40CrNiMo) is a non-magnetic Cobalt-Chromium-Nickel-Molybdenum alloy that combines very high strength and excellent formability, excellent corrosion resistance and high fatigue strenght. Typical composition C=0.15,NI=15.50,Co=40.00,Cr=20.00,Mo=7.00,Mn=2.00,Fe=remainder

R30003 Non-magnetic Cobalt-Chromium-Nickel-Molybdenum Alloy Cold Drawn Wire R30003 PHYNOX is an non-magnetic austenitic alloy strengthened by cold work and capable of additional hardening by aging at a moderate temperature (around 500°C). In the fully hardened condition, its elastic modulus is around 210 000 MPa, with UTS levels up to 2500 MPa on cold rolled strip. In addition to its very high yield strength, PHYNOX offers a range of physical, chemical and technological

Ni-Span-C Alloy 902 Constant Elastic Alloy Cold Drawn Wire in Stock NI-SPAN-C Alloy 902 is featured product of A-ONE ALLOY. In fact, when A-ONE ALLOY started its first business in special alloy area, the first product ordered is Ni-SPAN-C Alloy 902. Now A-ONE ALLOY's business covers 100+ products which is much more than what it is years ago. But it is not strange that A-ONE ALLOY has very strong strength in this product. The ingot stocked makes it possible to deliver forging

Ni-SPAN-C 902 is a precipitation hardenable NiFeCr alloy with a thermoelastic coefficient that can be controlled by the amount of cold work and heat treatment temperature to fit a specific application’s needs. Ni Span C 902 also has low magnetostrictive properties appropriate for specific applications and has been successfully utilized at cryogenic temperatures. Ni-Span-C 902 alloy is a good choice to produce Bourdon tube, as it has the characters as following Characters Good

NIMONIC alloy 90 (UNS N07090/W. Nr. 2.4632) is a NiCrCo base alloy with additions of titanium and aluminum, which makes its strength improved. It has been developed as an age-hardenable creepresisting alloy for service at temperatures up to 920°C. The alloy is used for exhaust reheaters, high-temperature spring, turbine blades, discs, forgings, ring sections and hot-working tools. Chemical composition Weight % Ni Cr Co Ti Al C Si Cu Fe Mn B S Zr Pb Alloy 90 Bal 18-21 15-21 2

UNS R30003 Material CoCrNiMo Alloy Cold Rolled Strip Mirror Finish for Diaphragm Valve Application R30003 is an non-magnetic austenitic alloy strengthened by cold work and capable of additional hardening by aging at a moderate temperature (around 500°C). In the fully hardened condition, its elastic modulus is around 210 000 MPa, with UTS levels up to 2500 MPa on cold rolled strip. In addition to its very high yield strength, R30003 offers a range of physical, chemical and

AMS 5225 UNS N09902 Iron-Nickel Alloy Strip Solution Heat Treated, Cold Rolled, 50% Reduction N09902 strip has been used typically for diaphragms, leaf springs, and helical springs, requiring a precipitation-hardenable alloy with a temperature coefficient of modulus of elasticity of -20 to +20 x 10-6 per degree Fahrenheit from -50 to +150 °F (-36 to +36 x 10-6 per degree Celsius from -46 to +66 °C) after suitable heat treatment, but usage is not limited to such applications.

R30003(Co40CrNiMo) is well known for its excellent resistance to corrosive environments, elevated temperature resistance and high strength. And it is non-magnetic. Its mechanical properties are often superior to stainless steel and other nickel alloys. There are arguments that in some (medical) applications, it offers several advantages versus titanium and thus considered a replacement of titanium. Chemical composition of Elgiloy(wt, %) Carbon ... 0.15 max Manganese 1.5-2.5

R30003(Co40CrNiMo) is well-known for its high hardness, high strength, ductility, exceptional formability, excellent corrosion resistance in harsh environments, high fatigue strength, and elevated temperature resistance. Spec ASTM F1058 AMS 5834 ISO 5832-7 AMS 5833 NACE MR0175 NOL-WS 13822 Equal grades UNS R30003 3J21 Phynox Elgiloy NAS604PH 2.4711 Chemical composition(wt, %) C Mn Si P S Co Cr Ni Mo Be Fe 0.15 max. 1.5-2.5 1.20 max. 0.015 max. 0.015 max 39.0-41.0 19.0-21.0 14

R30003 Co-Cr-Ni-Mo Cobalt Alloy Diaphragm for Diaphragm Valve Application R30003 Co-Cr-Ni-Mo Cobalt Alloy is an non-magnetic Austenitic alloy strengthened by cold work and capable of additional hardening by aging at a moderate temperature (around 500°C). In the fully hardened condition, its elastic modulus is around 210 000 MPa, with UTS levels up to 2500 MPa on cold rolled strip. In addition to its very high yield strength, R30003 offers a range of physical, chemical and

UNS R30008 is a wrought 40cobalt-20chromium-16iron-15nickel-7molybdenum alloy delivered in the form of wire and strip used for the manufacture of surgical implants. UNS R30008 provides the best solution whenever high mechanical performance is required under severely corrosive service conditions.The mechanical strength increases with cold rolling strain. Yield strengths higher than 1800 MPa can be achieved simply by cold working. Additional strengthening can be obtained by age

Xunshi New Material is pleased to provide our customer Phynox Super Elastic Alloy cold drawn wire. Diameter ranges from 0.20mm to 5.0mm. Our advantage is small MOQ and fast delivery. PHYNOX PHYNOX is an non-magnetic austenitic alloy strengthened by cold work and capable of additional hardening by aging at a moderate temperature (around 500°C). In the fully hardened condition, its elastic modulus is around 210 000 MPa, with UTS levels up to 2500 MPa on cold rolled strip. In