Stainless Steel Sheet And Coil

AISI 430 EN 1.4016 DIN X6Cr17 Stainless Steel Sheet Plate Strip Coil Grade 430 (1.4016) is the most common ferritic stainless steel. Type 430 stainless is one of the most widely used non-hardenable ferritic steel, with nominal 16% chromium it combines good corrosion resistance and heat and oxidation resistance up to 816℃ with good mechanical properities. Grade C Cr EN 1.4016, DIN X6Cr17 0.08 16.00~18.00 430 stainless grade combines the following characteristics: Fair

SiCromAl grades are a series of ferritic heat resisting stainless steels with varying amounts of silicon, chromium and aluminium. They are useful for temperatures up to 1150°C depending on grade. EN DINGrade C Si Cr Al 1.4713 X10CrAlSi7 0.08 0.8 6.5 0.8 1.4724 X10CrAlSi13 0.08 1.0 13.5 1.0 1.4742 X10CrAlSi18 0.08 1.3 18.0 1.0 1.4749 X18CrN28 0.1 1.0 27.0 0.2 1.4762 X10CrAlSi25 0.08 1.4

Martensitic stainless grade chromium molybdenum vanadium steels with 13 to 17 per cent chromium W.-nr. 1.4120 DIN X20CrMo13, it's same as BOEHLER SPECIAL STEEL STRIP T602. Typical applications: SEALING STRIPS ( X20CrMo13KG, Grade EN 1.4120 ) Chemical composition typical value% Grade C Cr Mo Ni X20CrMo13 0.220 13.27 0.90 0.16 Product forms Cold rolled stainless steel strip in coil, DIN 1.4120, Annealed,

Cold rolled sealing strip, Material number EN 1.4120, DIN X20CrMo13 annealed, bright surface, Cut edge, in Coil form. Typical thickness 0.25mm, 0.3mm, 0.6mm, 0.8mm etc. Chemical composition of grade X20CrMo13 C Si Mn P S Cr Mo Ni 0.17~0.22 1.00 max. 1.00 max. 0.040 max. 0.030 max. 12.00~14.00 0.9~1.3 1.00 max. Available forms EN 1.4120 DIN X20CrMo13 Stainless steel coil, slit strip, sheet ( plate ) For Details,

MARTENSITIC STAINLESS STEELS These steels of the 400 series usually contain a minimum of 11.5% up to 18% chromium and have higher levels of carbon than ferritics. They are capable of being heat treated to a wide range of useful hardness and strength levels, and are used extensively in cutlery, sports knives, multipurpose tools, and structural parts. Martensitic grade 410, chemical composition % C Cr 0.08~0.15 11

JIS SUS410L is a weldable ferritic stainless steel with elevated yield strength and resistance to abrasion. Its better corrosion resistance compared to carbon steels enables lower maintenance costs and longer service life. SUS410Lis a low-chromium structural ferritic stainless steel. Its corrosion resistance is limited in applications with increased corrosiveness. SUS410L can, however, replace carbon steel in many

Cold Rolled Stainless Steel Strip In Coil DIN1.4122 Grade X39CrMo17-1 Material No. W.-nr. 1.4122 ( DIN X39CrMo17-1 ) equals to DIN X38CrMo17, X38CrMo16, X35CrMo17 Stainless martensitic steel with very good wear, corrosion reistance and industrial polishability. Material W.-Nr. 1.4122 ( DIN X39CrMo17-1 ) is used for pump shafts, fitting and compressor parts, as well as steam and water control valves and boat shafts for use in fresh water. Products are delivered in soft

EN 1.4057 ( SUS431 ) Stainless Steel Plate For Spinneret Plate AISI EN, DIN GB JIS 431 1.4057 X20CrNi16-2 1Cr17Ni2 SUS431 Typical chemical composition % C Si Mn P S Cr Ni 0.19 0.25 0.40 0.025 0.001 15.9 1.6 Material 431 is a rust- and acid-resistant, martensitic chromium steel with nickel addition. Stainless 431 is designed to provide improved corrosion resistance and toughness in a quenchhardenable stainless steel. Mechanical properties include excellent toughness (impact

JIS G4305 cold rolled stainless steel sheet, plate and strip standard JIS SUS420J2, martensitic grade, increased hardness and strength when compared with type SUS410 stainless steel. SUS420J2 stainless chemical composition % C Cr 0.26~0.40 12.00~14.00 Available forms SUS420J2 stainless steel sheet, plate, coil and narrow strip For Details, please Contact WUXI GUANGLU Special Steel Co., Ltd. Stainless martensitic •

ASTM A176 AISI 431 ( UNS S43100 ) Cold Rolled Stainless Steel Sheets And Strips Martensitic grade AISI 431, UNS S43100, EN 1.4057, DIN X17CrNi16-2 ASTM A176 standard specification Stainless steel and heat resisting chromium steel plate, sheet and strip Chemical composition % C Si Mn P S Cr Ni 0.20 1.00 1.00 0.040 0.030 15.00~17.00 1.25~2.50 Product forms 431 stainless steel thin strip, sheet, plate For Details, please Contact WUXI GUANGLU Special Steel Co., Ltd. Stainless

Material AISI 410 ( EN 1.4006 ) Stainless Steel Sheet And Coil Martensitic grade 410, carbon content 0.08 ~ 0.15%, chromium 11.5 ~ 13.5% AISI 410, UNS S41000, EN 1.4006, DIN X12Cr13, JIS SUS410 Lower carbon content, when compared with AISI 420, JIS SUS420J1 ( 13% Cr - 0.2% C ) and SUS420J2 ( 13% Cr - 0.3% C ). Typical composition of grade 410 C Cr 0.12 11.65 Typical Mechanical property T.S. Rm Mpa Y.S. Rp0.2 Mpa EL A 50% HV 559 297 31 151 Product forms 410 ( 1.4006 )

AISI 431 , EN 1.4057 ( DIN X17CrNi16-2 ) Stainless Steel Sheet And Plate Grade 1.4057 is a corrosion and acid resistant martensitic chromium steel with nickel additive. The formation of chromium carbides and the associated chromium-depleted areas makes this material susceptible to intergranular corrosion. Main application in mechanical Engineering, petroleum and petrochemical industry and aviation. Material no. AISI/ASTM JIS EN/DIN GB 431, S43100 SUS431 1.4057, X17CrNi16-2

Type 431 is designed to provide improved corrosion resistance and toughness in a quench hardenable stainless steel. It has been used for parts such as aircraft fasteners and fittings and should be considered for structural members exposed to marine atmosphere. Mechanical properties include excellent toughness (impact strength) at relatively high hardness level. It offers the best corrosion resistance of the

17-4PH is a martensitic precipitation hardening stainless steel. 17-4PH stainless provides an outstanding combination of high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C), good toughness in both base metal and welds, and shorttime, low-temperature heat treatments that minimize warpage and scaling. 17-4PH stainless is widely used in the aerospace, chemical,

​ Material No. W.-nr. 1.4057 ( DIN X17CrNi16-2 ) = AISI 431, UNS S43100 = JIS SUS431 Grade AISI 431 nickel alloy stainless martensitic chromium steel, Heat treatable grade, capable of taking a mirror finish. Resistant to the action of water and steam, weak acids and alkaline solutions, as well as to acids and alkaline oxidizing effect such as nitric acid. Surface finish for optimum corrosion resistance: fine

AISI 440A 440B 440C Stainless Steel Sheet For Food Blades Knives Martensitic Stainless steel Type 440A, 440B, and 440C offer high hardness and tensile strength against fresh water, steam, petroleum spirits and alcohols. Hardenable high-carbon chromium steels designed to provide stainless properties with maximum hardness Have maximum hardness together with high strength and corrosion resistance in the hardened and stress relieved condition, Always used in the hardened or

405 is a 12% chromium stainless steel designed to be used in the as-welded condition. Unlike the other grades of 12% chromium stainless, 405 is not vulnerable to extensive hardening through air cooling from high temperatures. Specifications AISI/UNS EN/DIN JIS GB 405 S40500 1.4002 X6CrAl13 SUS405 0Cr13Al 06Cr13Al Chemical composition % weight C Cr Al 0.08 max 11.5~14.5 0.1~0.3 Applications Applications that

Grade 1.4923, High temperature resistant stainless steel with molybdenum addition. Grade C Cr Mo V Ni 1.4923 0.18~0.24 11.00~12.50 0.8~1.2 0.25~0.35 0.8~1.20 Applications Powerplant, Machine engineering, Power generation Components for pipe-lines, steam boilers and turbines Delivery forms X22CrMoV12-1 ( 1.4923 ) stainless coil and strip, cut sheets, plate For Details, please Contact WUXI GUANGLU Special

Grade 409, UNS S40900 is a stabilized ferritic general purpose stainless steel with 11% chromium. It is especially useful for applications requiring oxidation or corrosion protection beyond the capability of carbon steel and some coated steels. 409 has good oxidation resistance and formability, but lower corrosion resistance due to the chromium content. 409 is not as corrosion resistant as 304, 430 or 439

1.4509 is a low carbon, dual stabilised ferritic stainless steel. With 18% chromium, the steel has good corrosion resistance in moderately corrosive environments and good oxidation resistance at elevated temperatures. 1.4509 has good high temperature oxidation resistance and creep resistance and this makes it suitable for use in applications in automotive exhaust systems. Steel grades AISI UNS EN