Constant Velocity Joint

Dimension is (φ75-φ105) x (220-420) constant speed universal joint processing equipment CNC lathe, Its material choice is 40Cr, it forging shaft parts can be based on the use requirements, production type, equipment conditions and structure, the selection of bars, forgings and other blank form. For the axis with little difference in diameter of outer circle, rod material is generally the main material; Forgings are often used to save materials and reduce the workload of

Dimension is (φ75-φ105) x (220-420) constant velocity universal joint detection equipment has ultrasonic flaw detector, Its material choice is 40Cr, it this kind of alloy structure steel is suitable for medium precision and high speed shaft parts, this kind of steel after quenching and tempering, has good comprehensive mechanical properties. The surface hardness of bearing steel GCr15 and spring steel 65Mn can reach 50~58HRC after quenching and tempering, and they have high

The external dimension is (φ75-φ105) x (220-420) constant speed universal joint is cold finishing process, Its material choice is 40Cr, its forging shaft parts are often encountered in the machine one of the typical parts. It is mainly used to support transmission components, transfer torque and load. Shaft parts are rotating body parts, its length is greater than the diameter, generally by the concentric shaft cylindrical surface, conical surface, inner hole and thread and

Size is (φ75-φ105) x (220-420) constant speed universal joint is used in medium carbon steel, Its material choice is 40Cr, this kind of steel after tempering for manufacturing medium load and medium speed work of mechanical parts, such as car steering knuckle, half shaft and machine tools on the gear, shaft, worm, spline shaft, top sleeve, etc.; After quenching and tempering at medium temperature, it is used to manufacture parts that bear high load, impact and medium speed,

Constant Velocity joints with waste heat isothermal annealing weigh about 3.9kg,The material of this product is 40Cr, and its hardness after tempering is about 32-36HRC, that is to say, about 301-340Hb. Characteristic is that it belongs to medium carbon quenching and tempering steel, cold heading die steel. The steel is affordable and easy to process. After proper heat treatment, certain toughness, plasticity and wear resistance can be obtained. Normalizing can improve the

Constant Velocity joints with waste heat isothermal annealing weigh about 3.8kg,The material of this product is 40CR, and the standard steel number of GB in China is 40CR. [Specification for softening treatment of cold-pressed blank] Temperature 740~760℃, holding time 4~6h, and then at a cooling rate of 5~10℃/h, cooling to ≤600℃, out of the air cooling. Hardness ≤217HBW before treatment, hardness ≤163HBW after softening. [Specification for swinging tempering of scrap iron

Constant Velocity joints with waste heat isothermal annealing weigh about3.7kg,The material of this product is 40CR: China's GB standard steel number is 40Cr; German DIN standard material number 1.7035/1.7045, German DIN standard steel number 41CR4/42GR4; British EN standard steel Number 18, British BS standard steel number 41Cr4; French AFNOR standard steel 42C4, French NF standard steel 38CR4/41CR4; boundary dimension (φ75-φ105)x(220-420) weight 3.5-6.5Kg material 40Cr/CF53

Medium carbon steel processing Constant Velocity Joint weight is 2kg,The process flow of the product includes warm forging + heat treatment + cold finishing + machining, among which the machining process rules are one of the process documents that specify the machining process and operation methods of parts. Mechanical processing process rules generally include the following contents: the process route of workpiece processing, the specific content of each process and the

Medium carbon steel processing Constant Velocity Joint weight is 1.9kg,The process flow of the product includes warm forging + heat treatment + cold finishing + machining, among which the machining process rules are one of the process documents that specify the machining process and operation methods of parts. It is in the specific production conditions, the more reasonable process and operation methods, in accordance with the prescribed form of writing into the process

Medium carbon steel processing Constant Velocity Joint weight is 1.8kg,Its processing technology is warm forging + heat treatment + cold finishing + machining, among them, the operating procedures of machining are: 1.before the machine tool starts to observe the surrounding dynamic, after the machine tool starts, to stand in a safe position, in order to avoid the machine tool moving parts and iron splashing. 2.all kinds of machine tool operation, is not allowed to adjust the

Medium carbon steel processing Constant Velocity Joint weight is 1.6kg,Its processing technology is warm forging + heat treatment + cold finishing + machining, among them, the operating procedures of machining are: 1, where engaged in all kinds of machinery operators, must pass the safety technology training, examination, before the job. 2, before work according to the provisions of strict use of protective equipment, tie the cuffs, do not wear scarves, gloves, women should

Medium carbon steel processing Constant Velocity Joint weight is 1.6kg,Its processing technology has warm forging + heat treatment + cold finishing + machining, which machining workshop can use CAD/CAM(computer aided design computer aided manufacturing) system to nc machine tool automatic programming. The geometry of parts is automatically converted from CAD system to CAM system, and the machinist selects various machining methods on the virtual display screen. When the

Constant Velocity joints with waste heat isothermal annealing weigh about 1.5kg,The processing technology of this product includes warm forging + heat treatment + cold finishing + machining. Among them, machining is short for mechanical processing, which refers to the processing technology of removing materials by mechanical precise processing. Addition to seek quality, multiplication words production, drilling sets, processing necessities. Mechanical processing is mainly

Constant Velocity joints with waste heat isothermal annealing weigh about 1.4kg,The product is medium carbon steel, its strength, hardness is higher than low carbon steel, and the plasticity and toughness is lower than low carbon steel. Without heat treatment, directly use hot rolled material, cold drawn material, can also be used after heat treatment. The quenched and tempered medium carbon steel has good comprehensive mechanical properties. The highest hardness that can be

Constant Velocity joints with waste heat isothermal annealing weigh about3.6kg, The material of this product is 40Cr/CF53, among which 40Cr is the standard steel number of GB in China, and 40Cr steel is one of the most widely used steel in machinery manufacturing industry. After quenching and tempering, it has good comprehensive mechanical properties, good low temperature impact toughness and low notch sensitivity. Steel hardenability is good, water quenching can be quenched

Constant Velocity joints with waste heat isothermal annealing weigh about 1.4kg, The material used in this product is medium carbon steel, medium carbon steel refers to 0.25%~0.60% carbon steel, its hot working and cutting performance is good. According to the chemical composition of steel, it can be divided into carbon steel and alloy steel. Carbon steel is divided into: ①Low carbon steel, carbon content is less than 0.25%; ②Medium carbon steel, carbon content 0.25%--0.6%; ③

Constant Velocity joints with waste heat isothermal annealing weigh about 1.3kg, The product is medium carbon steel, its application in welding: Preheating is beneficial to reduce the highest hardness of the heat affected zone of carbon steel, to prevent cold cracks, which is the main process of welding carbon steel, preheating can improve joint plasticity, reduce residual stress after welding. Generally, the preheating temperature of 35 and 45 steel is 150~250℃ when the

Constant Velocity joints with isothermal annealing weigh 3.5Kg, The processing technology of this product is warm forging,Constant Velocity Joint is processed by warm forging, heat treatment, cold finishing and machining. Among them, warm forging refers to the forging of steel forgings with recrystallization temperature below and higher than normal temperature. The purpose of using warm forging process is to obtain precision forgings, warm forging is to improve the precision

Constant Velocity joints weighing is 3.5kg and are made of 40Cr/CF53, The heat treatment of the product is waste heat isothermal annealing, then what is waste heat isothermal annealing? Waste heat isothermal annealing refers to the process in which the forging billet is cooled to a certain temperature below Ac1 (generally 650℃) after stopping forging (generally 1000~1100℃), and the furnace is cooled to about 350℃ after holding for a certain period of time, and then comes out

Constant Velocity joints with waste heat isothermal annealing weigh about 1.2kg, The measuring equipment used for this product is Zeiss CMM,The main detection equipment of Constant Velocity Joint mainly includes three kinds of Zeiss CMM and Santoya profilometer. CMM is a kind of detector that can move in three directions, which can move on three mutually perpendicular guide rails. The detector transmits signals in contact or non-contact mode. The measurement function of CMM