2:1 Electrically Conductive RTV Epoxy Potting Compound For Transformers Fire Retardant High Temp
2:1 Epoxy Potting Compound For Transformers Power Module Insulation Sealing Led Driver RTV Potting Glue Fire Retardant High Temp Potting Epoxy Resin
Product Description
HN-5508 is widely used in transformers, resistors, filters, temperature sensors, temperature controllers, ignition coils, high voltage packs, aquarium equipment, anion generators, ultrasonic atomizers, and electronics and other components
HN-5508 epoxy resin at room temperature or low temperature, with low viscosity, long operation time, good fluidity, and easy penetration into the clearance of the product; no bubbles after curing, smooth surface, luster, high hardness
| uring | builder | Epoxy resin 5508 | Curing agent 5508 |
| pigment | Black / White et al | Ruburn / transparent surface | |
| A sticky epoxy resin water | r liquid specific | ||
| c gravity, g / cm3 | 1.4-1.5 | 1.05 | |
| Viscosity of 25℃ | 4,500—6,000cp s | 150—250cp storage | |
| e Period (25℃) | Six months | x months | |
|
processabili
|
mixing ratio | A: B =5:1 (weight ratio) | |
| Available for a time of 25℃ | 2-3H (100g mix) | ||
| curing time | 25℃ / 6-8H surface stem, 12-16H fully cured or 60-80℃/1.5-2H | ||
| After curing | 2 Tensile strength of kg/cm | 16-18 | |
| 2 Compressive strength of kg/cm | 18-22 | ||
| Resistance to the voltage of kv/mm | 20-22 | ||
| Surface resistance ofΩ-cm |
14 1.2*10 |
||
| Volume resistance ofΩ-cm |
15 1.1*10 |
||
| contraction percentage% | 0.35-0.55 | ||
| Water absorption rate was 25℃ * 24H | <0.03% | ||
| The hardness of SHORE A | 85-95 |
|
distortion temperature ℃ |
130-150 |
| low temperature resistant ℃ | -30 |