Mold Steel Plate

DIN 1.2311 Prehardened Mold Steel Plate For Large-sized Precision Plastic Mould Standard: GB/T 1299-19853. Similar grade: AISI-P20, DIN-1.2311, JIS-PDS-3, GB-3Cr2Mo Introdution: Grade P20 / 1.2311 is an internationally widely used plastic mold steel, its good mechanical properties, high hardenability can make Larger cross-section steel to obtain more uniform hardness, and this steel has good polishing performance and high mold surface finish. Chemical Composition(%): Grade C

Pre-hardened Mold Steel Plate 1.2738 / P20+Ni for Large Size Injection Mould Pre-hardened large size injection mould, can be pollished normally, used for making high demand large plastic mould. 1. Equivalent Grades GB DIN AISI ASSAB 3Cr2NiMnMo 1.2738 P20+Ni 718 2. Chemical Composition(%) Grade C Si Mn P S Cr Mo Ni P20+Ni 0.30-0.40 0.20-0.50 1.00-1.50 ≤0.030 ≤0.030 1.50-2.00 0.25-0.40 0.80-1.20 1.2738 0.35-0.45 0.20-0.40 1.30-1.60 ≤0.035 ≤0.035 1.80-2.10 0.15-0.25 0.90-1.20

Prehardening Plastic Mold Steel Plate For High Appearance Plastic Mould ► Similar grades: AISI-P21, JIS-, GB-B40 To make high pericision mirror plastic mould, high appearance home electronic plastic mould. ► Chemical composition (%): Grade C Si Mn P S Ni Mo Cu Al 0.06-0.20 ≤0.35 1.40-1.70 ≤0.030 ≤0.030 2.80-3.40 0.20-0.50 0.80-1.20 0.70-1.30 P21 0.10-0.18 ≤0.35 1.70-2.0 ≤0.030 ≤0.030 2.90-3.40 0.20-0.50 0.80-1.20 0.70-1.00 ► Introduction: is a pre

Hot Rolled Plastic Mold Steel Plate 1.3355 / T1 For Making Cutting Tools Equivalent grades: GB DIN AISI JIS W18Cr4V 1.3355 T1 SKH2 Available size(mm): Flat Bar Size(mm) Round bar Size(mm) Thickness Width Length Diameter Length 16-260 205-610 3000-6000 16-200 300-6000 Features: 1,High hardness, high red hardness and high temperature hardness, easy to grinding. 2,The application of the tool to work at a temperature of 600℃ can still keep cutting performance, such as vehicles,

1.2311 / P20 / 3Cr2Mo / PDS-3 Plastic Mold Steel Plate for Pre-hardened Injection Mold For high demand large-sized or medium-sized precision plastic mould and alloy parts. 1. Equivalnet grades: GB DIN AISI JIS 3CR2Mo 1.2311 P20 PDS-3 2. Chemical Composition(%) : C Si Mn Cr Mo S P Ni 0.28-0.40 0.20-0.80 0.60-1.00 1.40-2.00 0.30-0.55 ≤0.003 ≤0.030 0.05-0.10 3. Available size(mm): Plate Thickness (mm) Width (mm) Length (mm) 10-350 2000-2200 4000-12000 Block Thickness (mm) Width

Cold Work Mould Steel 1.2379 / SKD11 / D2 Hot Rolled Mold Steel Plate 1.2379 / SKD11 / D2 Hot Rolled Mold Steel , high wear resistance and micro deformation, cold working die steel, wind hard tool steel, carbon content up to 1.5%, chromium content high, noisy 11.5%, heat treatment, hardness up to 60HRC. D2 steel can be used to make large cross section, complex shape, strong impact, high resistance to cold working die steel, such as silicon steel sheet die, cold cutting

High Wear Resistance 1.2080 / D3 Cold Work Mold Flat Steel Introduction: Grade 1.2080 / SKD1 / D3 mold steel is one of a cold work mold steel with excellent wear resistance and stability heat treatment. Widely used for deep drawing die. The resistance welding electrode: Chromium, zirconimu, copper though the method combine with heat treatment and cold working to ensure is performance. So that it has the best mechanical property and good physical property. high carbon,high

Cold Work 1.2379 / D2 / SKD11 Plastic Mold Steel Plate For Making Cutting Tools Introduction D2 steel is a high wear resistant micro deformation cold working die steel, belonging to air hardening tool steel. With high quality fraction of carbon and high chronic, the hardness can up to 60HRC after heat treatment, but malleability,toughness,rust resistance is not good and the surface of the steel is also difficult to be polished. Chemical Composition(%): C Si Mn Cr Mo V P S 1

High Quality Forged 1.2738 Mold Steel Plate Pre-hardened HRC 30-36 1.2738 is a pre-hardened Plastic Mold Steel. Equivalent grades GB DIN AISI ASSAB 3Cr2NiMnMo 1.2738 P20+Ni 718 Chemical Composition(%) C Si Mn P S Cr Mo Ni 0.28-0.40 0.20-0.80 0.60-1.00 ≤0.03 ≤0.015 1.40-2.00 0.30-0.55 0.80-1.20 Hardness: Pre-hardened 33-37 HRC Applications 1) Suitable for molds with high gloss. 2) After the mold steel nitride surface hardness can reach 650 ~ 700HV, the number of products can

1.2316 Mold Steel Plate For Produce Chemical-resistant Plastic Mold 1.2316 mold steel is highly corrosion-resistant, high-polished pre-hardened plastic steel, excellent processing performance, excellent machinability. Excellent corrosion resistance Excellent polishing Excellent machinability Quenching with excellent stability 2316 Suitable for cosmetic molds, stationery molds and other need to polish the plastic mold requirements. 1. Grade GB DIN AISI JIS 4Cr16Mo 1.2316 420

High Tensile Hot Rolled SAE4140 / SCM440 / 1.7225 Mold Steel Plate SAE4140 mold steel plate is an alloy structural steel, it has good machinability, processing deformation is small, 4140 alloy structural steel fatigue resistance is quite good, is a medium hardenability steel. After heat treatment, it has good strength and good mechanical properties, good workmanship, high yield. The maximum temperature is 427 degrees Celsius. Equivalent grades GB(China) DIN(German) AISI(USA)

1.2311 P20 Prehardening Corrosion resistance Mold Steel Plate with Thickness 12-250mm Prehardening Wear Resistance Corrosion resistance mechanical behavior 1.2311 P20 Prehardening Corrosion resistance Plastic Mold Steel plate Material is a versatile, low-alloy tool steel that is characterized by good toughness at moderate strength levels. The special purpose Prehardening mold steel P20 steel plate is commonly used for plastic injection mold cavities and tooling and for die

1.2311 P20 Prehardening Mechanical Property Plastic Mold Steel Flat and Round Bar 1, Equivalent Grades: GB DIN AISI JIS 3Cr2Mo 1.2311 P20 PDS-3 2, Characteristics: a, Good hardenability b, Good integral machanical performance under high temperature c, Good heat-resistance and fatigue-resistance d, Good performance against liquid metal erosion e, High putity and homogeneous structure of China's biggest ESR production base for its strict requirement in the whole process of